Fabrication of Transparent and Conductive SWCNT/SiO<sub>2</sub> Composite Thin-Film by Photo-Irradiation of Molecular Precursor Films
A single-walled carbon nanotube (SWCNT)-silica composite thin film on a quartz glass was formed by ultraviolet irradiation (20–40 °C) onto a spin-coated precursor film. With 7.4 mass% SWCNTs, the electrical resistivity reached 7.7 × 10<sup>−3</sup> Ω·cm after UV-irradiation. The transmit...