Correlation of Lack of Fusion Pores with Stress Corrosion Cracking Susceptibility of L-PBF 316L: Effect of Surface Residual Stresses
Stress corrosion cracking (SCC) of laser powder bed fusion-fabricated 316L was studied under the variation in energy input density to emulate the existence of distinctive types of defects. Various electrochemical polarization measurements were performed in as-received polished and ground states, to...