Electrochemical corrosion behavior of tantalum coated 316L stainless steel by D.C. Magnetron sputtering for orthopedic applications
The austenitic stainless steel type 316L was engineered with a thin multilayer of tantalum with a thickness of 1.504µm, 3.893 µm and 6.083µm and a duration of 15, 30 and 60 minutes, respectively, by the DC Magnetron Sputtering. Electrochemical behaviors of all three samples were investigated by pote...