A Study on the Co-Content Optimization of the DD15 Single-Crystal Superalloy
The fourth-generation single-crystal superalloy DD15 with 6% Co, 9% Co and 12% Co was cast using the vacuum directionally solidified furnace, while other alloying element’s content remained unchanged. The long-term aging experiment was conducted at 1100 °C for 1000 h after standard heat treatment. T...