Enhanced high-temperature mechanical properties of the Cu–1.16Ni–0.36Cr alloy owing to interactions between metastable precipitates and dislocations
Herein, an alloy Cu–1.16Ni–0.36Cr with outstanding high-temperature mechanical properties was obtained, and the underlying mechanism was discussed. The properties were compared with those of commercial Cu–Fe–P alloys. The alloy exhibited a high-temperature softening temperature of 674.7 °C. Tensile...