316L Austenitic Stainless Steel Deformation Organization and Nitriding-Strengthened Layer Relationships
The organizational development of 316L austenitic stainless steel was examined in this work under various levels of compression deformation (0, 10%, 20%, 30%, 40%, and 50%) and thoroughly investigated at multiple scales using SEM and EBSD techniques. The 316L austenitic stainless steel was subjected...