Coercivity and Magnetic Anisotropy of (Fe<sub>0.76</sub>Si<sub>0.09</sub>B<sub>0.10</sub>P<sub>0.05</sub>)<sub>97.5</sub>Nb<sub>2.0</sub>Cu<sub>0.5</sub> Amorphous and Nanocrystalline Alloy Produced by Gas Atomization Process

Coercivity and Magnetic Anisotropy of (Fe<sub>0.76</sub>Si<sub>0.09</sub>B<sub>0.10</sub>P<sub>0.05</sub>)<sub>97.5</sub>Nb<sub>2.0</sub>Cu<sub>0.5</sub> Amorphous and Nanocrystalline Alloy Produced by Gas Atomization Process

We present the evolution of magnetic anisotropy obtained from the magnetization curve of (Fe<sub>0.76</sub>Si<sub>0.09</sub>B<sub>0.10</sub>P<sub>0.05</sub>)<sub>97.5</sub>Nb<sub>2.0</sub>Cu<sub>0.5</sub> amorphous a...

সম্পূর্ণ বিবরণ

গ্রন্থ-পঞ্জীর বিবরন
প্রধান লেখক: Kenny L. Alvarez, José Manuel Martín, Nerea Burgos, Mihail Ipatov, Lourdes Domínguez, Julián González
বিন্যাস: প্রবন্ধ
ভাষা:English
প্রকাশিত: MDPI AG 2020-05-01
মালা:Nanomaterials
বিষয়গুলি:
gas atomization
amorphous and nanocrystalline materials
magnetic characterization
anisotropy field
soft magnetic materials
অনলাইন ব্যবহার করুন:https://www.mdpi.com/2079-4991/10/5/884

আন্তর্জাল

https://www.mdpi.com/2079-4991/10/5/884

অনুরূপ উপাদানগুলি