Hydrogenation of Carboxyl Nitrile Butadiene Rubber Latex Using a Ruthenium-Based Catalyst
Hydrogenated carboxyl nitrile rubber (HXNBR) is endowed with superior mechanical performance and heat–oxygen aging resistance via emulsion hydrogenation of its precursor, i.e., carboxyl nitrile rubber (XNBR). Herein, a ruthenium-based catalyst was prepared to achieve the direct catalytic hydrogenati...