FE simulation on fatigue failure due to cracks initiated at corrosion zone
Deep-sea pipelines are subject to large plastic strains due to reeling installation methods.. While these pipelines can withstand small cracks generated during installation, cyclic loading in the deep-sea environment causes cracks to grow and merge, leading to fatigue failure. The corrosion zone i...