PENGARUH TEMPERATUR TUANG DAN KANDUNGAN SILIKON TERHADAP CACAT HOT TEARING PADA PENGECORAN PADUAN Al-Si DENGAN CETAKAN CRCM VERTIKAL
Aluminium alloys can not be separated from a variety of defects that occur during the casting such as porosity, shrinkage, hot tearing, small holes, misrun and blister. The defects occur in foundry products are usually caused by poor mixing, improper casting, which is too rapid freezing and mold des...