Microstructural degradation of polycrystalline superalloys from oxidized carbides and implications on crack initiation
Surface connected carbides in a polycrystalline superalloy oxidized at 750 °C in air were studied as potential crack initiation sites. Lattice rotations measured in the γ/γ′ grains using high-resolution electron backscatter diffraction enabled investigation of the plastic deformation induced solely...