LaSrCo0.5Rh0.5O3.25 and LaSrNi0.5Rh0.5O3.25:topochemically reduced, mixed valence Rh(I)/Rh(III) Oxides
Topochemical reduction of the n = 1 Ruddlesden-Popper phases LaSrCo0.5Rh0.5O4 and LaSrNi0.5Rh0.5O4 with Zr yields LaSrCo0.5Rh0.5O3.25 and LaSrNi0.5Rh0.5O3.25, respectively. Magnetization and XPS data reveal that while the rhodium centers in LaSrCo0.5Rh0.5O3.25 and LaSrNi0.5Rh0.5O3.25 have an average...