Rates of intergranular environment assisted cracking in three-dimensional model microstructures

Rates of intergranular environment assisted cracking in three-dimensional model microstructures

Microstructure can have a significant effect on the materials' resistance to intergranular environment assisted cracking. Certain grain boundaries are susceptible to degradation by stress corrosion while others have high resistance, and it is recognised that increasing the fraction of resistant...

Полное описание

Библиографические подробности
Главные авторы:	Jivkov, A, Marrow, T
Формат:	Journal article
Язык:	English
Опубликовано:	2007

Схожие документы

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
по: Jivkov, A, и др.
Опубликовано: (2007)

A three-dimensional computational model for intergranular cracking
по: Jivkov, A, и др.
Опубликовано: (2006)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
по: Jivkov, A, и др.
Опубликовано: (2005)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
по: Jivkov, A, и др.
Опубликовано: (2008)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
по: Jivkov, A, и др.
Опубликовано: (2008)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
по: Jivkov, A, и др.
Опубликовано: (2006)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
по: Marrow, T, и др.
Опубликовано: (2006)

Intergranular stress corrosion crack propagation in sensitised austenitic stainless steel (microstructure modelling and experimental observation)
по: Marrow, T, и др.
Опубликовано: (2006)

Intergranular crack nucleation in polycrystalline alumina
по: Aswad, M, и др.
Опубликовано: (2010)

Intergranular crack nucleation in polycrystalline alumina
по: Aswad, M, и др.
Опубликовано: (2010)

Intergranular crack nuclei in polycrystalline alumina
по: Aswad, M, и др.
Опубликовано: (2012)

Intergranular crack nuclei in polycrystalline alumina
по: Aswad, M, и др.
Опубликовано: (2012)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
по: Duff, J, и др.
Опубликовано: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
по: Zhang, Y, и др.
Опубликовано: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
по: Zhang, Y, и др.
Опубликовано: (2009)

In-situ observation and modelling of intergranular cracking in polycrystalline alumina
по: Marrow, T, и др.
Опубликовано: (2011)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
по: Rahimi, S, и др.
Опубликовано: (2008)

New techniques for intergranular stress corrosion crack observation
по: Marrow, T, и др.
Опубликовано: (2008)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
по: Kovac, J, и др.
Опубликовано: (2012)

Grain boundary engineering for crack bridging: A new model for intergranular stress corrosion crack (IGSCC) propagation
по: Engelberg, D, и др.
Опубликовано: (2008)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
по: King, A, и др.
Опубликовано: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
по: Rahimi, S, и др.
Опубликовано: (2019)

Towards modelling intergranular stress-corrosion cracks using experimentally obtained grain topologies
по: Simonovski, I, и др.
Опубликовано: (2010)

Stress assisted intergranular oxidation cracking of Incoloy Alloy 908
по: Morra, M.M.
Опубликовано: (2015)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
по: S. Rahimi, и др.
Опубликовано: (2020-02-01)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
по: Rahimi, S, и др.
Опубликовано: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
по: Rahimi, S, и др.
Опубликовано: (2009)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
по: Babout, L, и др.
Опубликовано: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
по: Babout, L, и др.
Опубликовано: (2006)

Cracks in refractory concrete: Transgranular or intergranular?
по: Christian Jung, и др.
Опубликовано: (2025-02-01)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
по: Rahimi, S, и др.
Опубликовано: (2016)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
по: Janaszewski, M, и др.
Опубликовано: (2007)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
по: Rahimi, S, и др.
Опубликовано: (2012)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
по: Rahimi, S, и др.
Опубликовано: (2012)

Calculation of Hydrogen Buildup in the Neighborhood of Intergranular Cracks
по: Zohdi, T.I., и др.
Опубликовано: (1998-03-01)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
по: Huang, Y, и др.
Опубликовано: (2001)

Experimental validation of intergranular stress corrosion cracking predictive models
по: Saravanan, N
Опубликовано: (2022)

Correlations of electrochemical noise, acoustic emission and complementary monitoring techniques during intergranular stress-corrosion cracking of austenitic stainless steel
по: Kovac, J, и др.
Опубликовано: (2010)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
по: Stratulat, A, и др.
Опубликовано: (2014)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
по: Stratulat, A, и др.
Опубликовано: (2014)