Rates of intergranular environment assisted cracking in three-dimensional model microstructures

Rates of intergranular environment assisted cracking in three-dimensional model microstructures

Microstructure can have a significant effect on the materials' resistance to intergranular environment assisted cracking. Certain grain boundaries are susceptible to degradation by stress corrosion while others have high resistance, and it is recognised that increasing the fraction of resistant...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Jivkov, A, Marrow, T
Định dạng:	Journal article
Ngôn ngữ:	English
Được phát hành:	2007

Những quyển sách tương tự

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
Bằng: Jivkov, A, et al.
Được phát hành: (2007)

A three-dimensional computational model for intergranular cracking
Bằng: Jivkov, A, et al.
Được phát hành: (2006)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
Bằng: Jivkov, A, et al.
Được phát hành: (2005)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
Bằng: Jivkov, A, et al.
Được phát hành: (2008)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
Bằng: Jivkov, A, et al.
Được phát hành: (2008)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
Bằng: Jivkov, A, et al.
Được phát hành: (2006)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
Bằng: Marrow, T, et al.
Được phát hành: (2006)

Intergranular stress corrosion crack propagation in sensitised austenitic stainless steel (microstructure modelling and experimental observation)
Bằng: Marrow, T, et al.
Được phát hành: (2006)

Intergranular crack nucleation in polycrystalline alumina
Bằng: Aswad, M, et al.
Được phát hành: (2010)

Intergranular crack nucleation in polycrystalline alumina
Bằng: Aswad, M, et al.
Được phát hành: (2010)

Intergranular crack nuclei in polycrystalline alumina
Bằng: Aswad, M, et al.
Được phát hành: (2012)

Intergranular crack nuclei in polycrystalline alumina
Bằng: Aswad, M, et al.
Được phát hành: (2012)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
Bằng: Duff, J, et al.
Được phát hành: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
Bằng: Zhang, Y, et al.
Được phát hành: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
Bằng: Zhang, Y, et al.
Được phát hành: (2009)

In-situ observation and modelling of intergranular cracking in polycrystalline alumina
Bằng: Marrow, T, et al.
Được phát hành: (2011)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
Bằng: Rahimi, S, et al.
Được phát hành: (2008)

New techniques for intergranular stress corrosion crack observation
Bằng: Marrow, T, et al.
Được phát hành: (2008)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
Bằng: Kovac, J, et al.
Được phát hành: (2012)

Grain boundary engineering for crack bridging: A new model for intergranular stress corrosion crack (IGSCC) propagation
Bằng: Engelberg, D, et al.
Được phát hành: (2008)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
Bằng: King, A, et al.
Được phát hành: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
Bằng: Rahimi, S, et al.
Được phát hành: (2019)

Towards modelling intergranular stress-corrosion cracks using experimentally obtained grain topologies
Bằng: Simonovski, I, et al.
Được phát hành: (2010)

Stress assisted intergranular oxidation cracking of Incoloy Alloy 908
Bằng: Morra, M.M.
Được phát hành: (2015)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
Bằng: S. Rahimi, et al.
Được phát hành: (2020-02-01)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
Bằng: Rahimi, S, et al.
Được phát hành: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
Bằng: Rahimi, S, et al.
Được phát hành: (2009)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
Bằng: Babout, L, et al.
Được phát hành: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
Bằng: Babout, L, et al.
Được phát hành: (2006)

Cracks in refractory concrete: Transgranular or intergranular?
Bằng: Christian Jung, et al.
Được phát hành: (2025-02-01)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
Bằng: Rahimi, S, et al.
Được phát hành: (2016)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
Bằng: Janaszewski, M, et al.
Được phát hành: (2007)

Oxidation assisted intergranular cracking in 718 Nickel Superalloy: on the mechanism of dynamic embrittlement
Bằng: Amanda de Vasconcelos Varela, et al.
Được phát hành: (2018-07-01)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
Bằng: Rahimi, S, et al.
Được phát hành: (2012)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
Bằng: Rahimi, S, et al.
Được phát hành: (2012)

Calculation of Hydrogen Buildup in the Neighborhood of Intergranular Cracks
Bằng: Zohdi, T.I., et al.
Được phát hành: (1998-03-01)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
Bằng: Huang, Y, et al.
Được phát hành: (2001)

Experimental validation of intergranular stress corrosion cracking predictive models
Bằng: Saravanan, N
Được phát hành: (2022)

Correlations of electrochemical noise, acoustic emission and complementary monitoring techniques during intergranular stress-corrosion cracking of austenitic stainless steel
Bằng: Kovac, J, et al.
Được phát hành: (2010)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
Bằng: Stratulat, A, et al.
Được phát hành: (2014)