Engineering coercivity in YFe2 dominated DyFe2/YFe2 superlattice by patterning
Single crystal 400 nm thick Laves phase [20 Å∈DyFe 2/80 Å∈YFe2]40 superlattice have been grown by MBE with a (110) growth direction. VSM measurements performed at room temperature with an applied field range of ±1.2×105 Oe, directed along the [001] direction, reveal a unique single-phase-liked ferri...