In-situ annealing of self-ion irradiation damage in tungsten

In our earlier work [1] microstructural evolution in tungsten under self-ion irradiation was investigated as a function of temperature and dose by in-situ 150 keV W+ ion irradiations on the IVEM-Tandem facility at Argonne National Laboratory (ANL). The present work focuses on the thermal stability o...