Intergranular crack tip oxidation in a Ni-base superalloy

Intergranular crack tip oxidation in a Ni-base superalloy

Weitere Versionen anzeigen (1)

High-temperature intergranular crack tip oxidation under a single 600 s long sustained tensile load at 700 °C was studied for the Ni-base superalloy Allvac 718Plus. High-resolution analytical techniques showed oxidation to take place at and immediately ahead of the tip of an open crack, forming a cl...

Ausführliche Beschreibung

Bibliographische Detailangaben
Hauptverfasser:	Viskari, L, Hornqvist, M, Moore, K, Cao, Y, Stiller, K
Format:	Journal article
Sprache:	English
Veröffentlicht:	2013

Ähnliche Einträge

Intergranular crack tip oxidation in a Ni-base superalloy
von: Viskari, L, et al.
Veröffentlicht: (2013)

High-temperature crack growth in a Ni-base superalloy during sustained load
von: Hornqvist, M, et al.
Veröffentlicht: (2014)

Oxidation assisted intergranular cracking in 718 Nickel Superalloy: on the mechanism of dynamic embrittlement
von: Amanda de Vasconcelos Varela, et al.
Veröffentlicht: (2018-07-01)

Meta-Dynamic Recrystallization in the Ni-Based Superalloy Haynes 282
von: Emil Eriksson, et al.
Veröffentlicht: (2023-07-01)

Strain field measurement around the crack tip in Ni-base superalloy using Digital Image Correlation
von: Yuki OTSUKA, et al.
Veröffentlicht: (2018-09-01)

Stress assisted intergranular oxidation cracking of Incoloy Alloy 908
von: Morra, M.M.
Veröffentlicht: (2015)

Intergranular crack nucleation in polycrystalline alumina
von: Aswad, M, et al.
Veröffentlicht: (2010)

Intergranular crack nuclei in polycrystalline alumina
von: Aswad, M, et al.
Veröffentlicht: (2012)

Intergranular crack nucleation in polycrystalline alumina
von: Aswad, M, et al.
Veröffentlicht: (2010)

Intergranular crack nuclei in polycrystalline alumina
von: Aswad, M, et al.
Veröffentlicht: (2012)

Macro- and micro-mechanical behaviour of a γ′ strengthened Ni-based superalloy at cryogenic temperatures
von: Nitesh Raj Jaladurgam, et al.
Veröffentlicht: (2021-11-01)

Cracks in refractory concrete: Transgranular or intergranular?
von: Christian Jung, et al.
Veröffentlicht: (2025-02-01)

Visualizing oxygen transport pathways during intergranular oxidation in Ni-Cr
von: Martin Weiser, et al.
Veröffentlicht: (2023-08-01)

Reductions of Intergranular Corrosion Resistance and Wear Resistance in a Ni-Cr-Mo-Based Superalloy by Aging-Treatment-Induced Precipitation
von: Pengyan Zhang, et al.
Veröffentlicht: (2021-08-01)

Grain Boundary Engineering and Its Effect on Intergranular Corrosion Resistance of a Ni-Cr-Mo Based C276 Superalloy
von: Chi Zhang, et al.
Veröffentlicht: (2022-11-01)

The influence of intergranular oxidation on surface crack formation in continuous casting of steel
von: Georg Gaiser, et al.
Veröffentlicht: (2023-09-01)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
von: Duff, J, et al.
Veröffentlicht: (2009)

Calculation of Hydrogen Buildup in the Neighborhood of Intergranular Cracks
von: Zohdi, T.I., et al.
Veröffentlicht: (1998-03-01)

Effects of Re, W and Co on dislocation nucleation at the crack tip in the γ-phase of Ni-based single-crystal superalloys by atomistic simulation
von: Dianwu Wang, et al.
Veröffentlicht: (2019-07-01)

3D modelling of intergranular stress corrosion cracking (IGSCC)
von: Zhang, Y, et al.
Veröffentlicht: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
von: Zhang, Y, et al.
Veröffentlicht: (2009)

In-situ observation and modelling of intergranular cracking in polycrystalline alumina
von: Marrow, T, et al.
Veröffentlicht: (2011)

Simulation of oxidation-nitridation-induced microstructural degradation in a cracked Ni-based superalloy at high temperature
von: Yuan Kang, et al.
Veröffentlicht: (2014-01-01)

Oxygen changes crack modes of Ni-based single crystal superalloy
von: Xueqiao Li, et al.
Veröffentlicht: (2021-12-01)

Crack Initiation in Ni-Based Single Crystal Superalloy under Low-Cycle Fatigue-Oxidation Conditions
von: Pengfei Wang, et al.
Veröffentlicht: (2023-11-01)

A three-dimensional computational model for intergranular cracking
von: Jivkov, A, et al.
Veröffentlicht: (2006)

New techniques for intergranular stress corrosion crack observation
von: Marrow, T, et al.
Veröffentlicht: (2008)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
von: Jivkov, A, et al.
Veröffentlicht: (2005)

Detection of Sensitization and Intergranular Corrosion of Fe-Cr-Ni Alloys
von: Kain, V., et al.
Veröffentlicht: (1997-07-01)

Intergranular Grooving During Oxidation of Intermetallics
von: Katsman, A., et al.
Veröffentlicht: (1996-07-01)

Additive manufacturing of Ni-based superalloys: Residual stress, mechanisms of crack formation and strategies for crack inhibition
von: Chuan Guo, et al.
Veröffentlicht: (2023-03-01)

The effects of intergranular carbides on the grain boundary oxidation and cracking in a cold-worked Alloy 600
von: Shen, Z, et al.
Veröffentlicht: (2019)

Experimental validation of intergranular stress corrosion cracking predictive models
von: Saravanan, N
Veröffentlicht: (2022)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
von: Huang, Y, et al.
Veröffentlicht: (2001)

The cracking behavior of the new Ni-based superalloy GH4151 in the triple melting process
von: Lei Jia, et al.
Veröffentlicht: (2023-07-01)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
von: King, A, et al.
Veröffentlicht: (2008)

On the role of intergranular nanocavities in long-term stress corrosion cracking of Alloy 690
von: Shen, Z, et al.
Veröffentlicht: (2021)

Data-driven Bayesian model-based prediction of fatigue crack nucleation in Ni-based superalloys
von: Maxwell Pinz, et al.
Veröffentlicht: (2022-03-01)

Hydrogen-Induced Intergranular Fracture Behavior Accelerated by Needle-like MC Carbide in IN740H Superalloy
von: Seung-Yong Lee, et al.
Veröffentlicht: (2022-11-01)

Microstructural and intergranular corrosion properties of Inconel 625 superalloys fabricated using wire arc additive manufacturing
von: Chun Guo, et al.
Veröffentlicht: (2021-01-01)