Intergranular crack tip oxidation in a Ni-base superalloy
High-temperature intergranular crack tip oxidation under a single 600 s long sustained tensile load at 700 °C was studied for the Ni-base superalloy Allvac 718Plus. High-resolution analytical techniques showed oxidation to take place at and immediately ahead of the tip of an open crack, forming a cl...