A study on the diffusion-induced grain boundary migration ahead of stress corrosion cracking crack tips through advanced characterization

Three austenitic alloys with different Ni content were stress corrosion cracking (SCC) tested in simulated pressurized water reactor (PWR) primary water at 320 and 360ºC. Diffusion-induced grain boundary migration (DIGM) associated with preferential intergranular oxidation (PIO) is observed ahead of...

Повний опис

Бібліографічні деталі
Автори: Shen, Z, Arioka, K, Lozano-Perez, S
Формат: Journal article
Мова:English
Опубліковано: Elsevier 2021