Ductile deformation in alumina/silicon carbide nanocomposites

Ductile deformation in alumina/silicon carbide nanocomposites

A transmission electron microscope study on cross sections obtained from ground and polished surfaces has revealed that ductile deformation is dominated by dislocations in alumina/silicon carbide nanocomposites containing 1, 5 and 10 vol% silicon carbide particles, and by twinning in unreinforced al...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Wu, H, Roberts, S, Derby, B
Định dạng:	Journal article
Ngôn ngữ:	English
Được phát hành:	2010

Những quyển sách tương tự

Residual stress and subsurface damage in machined alumina and alumina/silicon carbide nanocomposite ceramics
Bằng: Wu, H, et al.
Được phát hành: (2001)

Crack healing in an alumina/silicon carbide nanocomposite after grinding and annealing
Bằng: Wu, H, et al.
Được phát hành: (2000)

Subsurface damage in alumina and alumina-silicon carbide nanocomposites
Bằng: Tanner, B, et al.
Được phát hành: (2004)

Residual stress determination and subsurface microstructure in ground and polished alumina/silicon carbide nanocomposites and monolithic alumina ceramics
Bằng: Wu, H, et al.
Được phát hành: (2000)

Sub-surface damage in ground and annealed alumina and alumina-silicon carbide nanocomposites
Bằng: Tanner, B, et al.
Được phát hành: (2006)

Alumina/silicon carbide nanocomposites
Bằng: Todd, R
Được phát hành: (2005)

Polishing behavior and surface quality of alumina and alumina/silicon carbide nanocomposites
Bằng: Kara, H, et al.
Được phát hành: (2000)

Polishing and wear behaviour of sintered alumina-silicon carbide nanocomposites
Bằng: Cock, A, et al.
Được phát hành: (2001)

Effects of yttrium on the sintering and microstructure of alumina-silicon carbide "nanocomposites"
Bằng: Cock, A, et al.
Được phát hành: (2005)

Thermal shock resistance of sintered alumina/silicon carbide nanocomposites evaluated by indentation techniques
Bằng: Maensiri, S, et al.
Được phát hành: (2002)

Wear Behavior of Graphene-Reinforced Alumina–Silicon Carbide Whisker Nanocomposite
Bằng: Anton Smirnov, et al.
Được phát hành: (2019-01-01)

Erosive wear of alumina/SiC nanocomposite ceramics
Bằng: Lawrence, C, et al.
Được phát hành: (1999)

Ductile grinding of Silicon carbide in high speed grinding
Bằng: Chongjun WU, et al.
Được phát hành: (2016-04-01)

The wet erosive wear of polycrystalline alumina with silicon carbide particulate inclusions
Bằng: Twigg, P, et al.
Được phát hành: (1997)

Tribological Characteristics of Silicon Carbide – Epoxy Nanocomposites
Bằng: Bahjat B. Kadhim
Được phát hành: (2017-11-01)

Spark plasma sintering of alumina/yttria‐doped silicon carbide
Bằng: Antonio Popolizio, et al.
Được phát hành: (2020-03-01)

Ductile deformation in alumina ceramics under quasi-static to dynamic contact impact
Bằng: Robert G. Crookes, et al.
Được phát hành: (2020-02-01)

Evaluation of the self-healing capacity of ceramics produced with alumina and silicon carbide
Bằng: N. R. de Souza, et al.
Được phát hành: (2022-07-01)

Residual stress distribution in a functionally graded alumina-silicon carbide material
Bằng: Dancer, C, et al.
Được phát hành: (2012)

Residual stress distribution in a functionally graded alumina-silicon carbide material
Bằng: Dancer, C, et al.
Được phát hành: (2012)

Densification studies of silicon carbide-based ceramics with yttria, silica and alumina as sintering additives
Bằng: J. Marchi, et al.
Được phát hành: (2001-10-01)

BRITTLE TO DUCTILE TRANSITION IN SILICON.
Bằng: Samuels, J, et al.
Được phát hành: (1986)

THE BRITTLE DUCTILE TRANSITION IN SILICON
Bằng: Hirsch, P, et al.
Được phát hành: (1991)

THE BRITTLE-TO-DUCTILE TRANSITION IN SILICON
Bằng: Samuels, J, et al.
Được phát hành: (1988)

HIGH-TEMPERATURE MICROHARDNESS STUDY OF THE BRITTLE-DUCTILE TRANSITION IN TITANIUM CARBIDE
Bằng: Serbena, F, et al.
Được phát hành: (1995)

Sintering temperature-microstructure-property relationships of alumina matrix composites with silicon carbide and silica additives
Bằng: Limpichaipanit Apichart, et al.
Được phát hành: (2017-07-01)

Biocompatibility Study of A Hydroxyapatite-Alumina and Silicon Carbide Composite Scaffold for Bone Tissue Engineering
Bằng: Mohammad Saki, et al.
Được phát hành: (2009-01-01)

Effect of ion irradiation on nanoindentation fracture and deformation in silicon carbide
Bằng: Leide, AJ, et al.
Được phát hành: (2021)

Current Status of Carbidic Austempered Ductile Iron
Bằng: Yang Penghui, et al.
Được phát hành: (2022-01-01)

Carbidic Bainitic and Ausferritic Ductile Cast Iron
Bằng: Gumienny G.
Được phát hành: (2013-12-01)

The brittle-ductile transition in silicon. I. experiments
Bằng: Samuels, J, et al.
Được phát hành: (1989)

Corrosion behavior and resistance parameters of silicon carbide nanocomposite coating on different metals
Bằng: M.J. Suriani, et al.
Được phát hành: (2018-03-01)

The brittle-ductile transition in silicon. II. interpretation
Bằng: Hirsch, P, et al.
Được phát hành: (1989)

Effect of residual compressive surface stress on severe wear of alumina-silicon carbide two-layered composites
Bằng: Dancer, C.E.J., et al.
Được phát hành: (2014)

Study of Nano-Titania Addition on Mechanical Strength of Mullite-Bonded Alumina-Silicon Carbide Nano-Composites
Bằng: N. Zakeri, et al.
Được phát hành: (2015-12-01)

Study of Nano-Titania Addition on Mechanical Strength of Mullite-Bonded Alumina-Silicon Carbide Nano-Composites
Bằng: N. Zakeri, et al.
Được phát hành: (2015-12-01)

Subsurface damage analysis by TEM and 3D FIB crack mapping in alumina and alumina/5vol.%SiC nanocomposites
Bằng: Wu, H, et al.
Được phát hành: (2003)

Silicon carbide /
Bằng: 269121 Frantsevich, I. N., et al.
Được phát hành: (1970)

Synthesis Of Polycrystalline Silicon Carbide Using Aluminum Carbide And Calcium Carbide With Silicon Tetrachloride
Bằng: Ruzlan, Muhammad Hakim
Được phát hành: (2018)

Compressive deformation of liquid phase-sintered porous silicon carbide ceramics
Bằng: Taro Shimonosono, et al.
Được phát hành: (2014-12-01)