Self-organization of nanoneedles in Fe/GaAs (001) epitaxial thin film
Well-aligned nanoneedles are found to form in a FeGaAs (001) epitaxial thin film when irradiated with a Ga+ ion beam normal to the sample surface at an ion dose of 3× 1017 cm2 in a focused ion beam. These nanoneedles, with their axes perpendicular to the original sample surface, are composed of GaAs...
मुख्य लेखकों: | Huang, Y, Wang, S, Wang, C, Xie, Z, Cockayne, D, Ward, R |
---|---|
स्वरूप: | Journal article |
भाषा: | English |
प्रकाशित: |
2006
|
समान संसाधन
-
Magnetic anisotropy of half-metallic Co2FeAl ultra-thin films epitaxially grown on GaAs(001)
द्वारा: Bolin Lai, और अन्य
प्रकाशित: (2019-06-01) -
Variable-temperature micromagnetic study of epitaxially grown MnAs films on GaAs(001)
द्वारा: Mohanty, J, और अन्य
प्रकाशित: (2003) -
Selective etching of epitaxial MnAs films on GaAs(001): Influence of structure and strain
द्वारा: Mohanty, J, और अन्य
प्रकाशित: (2005) -
Temperature-dependent magnetic force microscopy investigation of epitaxial MnAs films on GaAs(001)
द्वारा: Plake, T, और अन्य
प्रकाशित: (2003) -
Capacitance-voltage measurements in GaAs thin-film epitaxial structures
द्वारा: Gorev N. B., और अन्य
प्रकाशित: (2009-10-01)