Intergranular crack nuclei in polycrystalline alumina

Intergranular crack nuclei in polycrystalline alumina

Show other versions (1)

Digital image correlation has been applied to optical images in order to detect crack nuclei in fine-grain size pure and Cr-doped aluminas. Individual intergranular crack nuclei within areas comprising tens of thousands of grains were detectable, and their crack lengths and opening strains obtained...

Disgrifiad llawn

Manylion Llyfryddiaeth
Prif Awduron:	Aswad, M, Marrow, T
Fformat:	Journal article
Iaith:	English
Cyhoeddwyd:	Elsevier 2012

Eitemau Tebyg

Intergranular crack nuclei in polycrystalline alumina
gan: Aswad, M, et al.
Cyhoeddwyd: (2012)

Intergranular crack nucleation in polycrystalline alumina
gan: Aswad, M, et al.
Cyhoeddwyd: (2010)

Intergranular crack nucleation in polycrystalline alumina
gan: Aswad, M, et al.
Cyhoeddwyd: (2010)

In-situ observation and modelling of intergranular cracking in polycrystalline alumina
gan: Marrow, T, et al.
Cyhoeddwyd: (2011)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
gan: Duff, J, et al.
Cyhoeddwyd: (2009)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
gan: Vertyagina, Y, et al.
Cyhoeddwyd: (2014)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
gan: Vertyagina, Y, et al.
Cyhoeddwyd: (2014)

Direct observations of electrochemically induced intergranular cracking in polycrystalline NMC811 particles
gan: Parks, HCW, et al.
Cyhoeddwyd: (2022)

A three-dimensional computational model for intergranular cracking
gan: Jivkov, A, et al.
Cyhoeddwyd: (2006)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
gan: Jivkov, A, et al.
Cyhoeddwyd: (2005)

Acoustic emission and crack propagation in polycrystalline alumina /
gan: Evans, Anthony G. (Anthony Glyn), 1942-

Diffraction contrast tomography of polycrystalline alumina
gan: Marrow, T, et al.
Cyhoeddwyd: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
gan: Zhang, Y, et al.
Cyhoeddwyd: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
gan: Zhang, Y, et al.
Cyhoeddwyd: (2009)

Rates of intergranular environment assisted cracking in three-dimensional model microstructures
gan: Jivkov, A, et al.
Cyhoeddwyd: (2007)

New techniques for intergranular stress corrosion crack observation
gan: Marrow, T, et al.
Cyhoeddwyd: (2008)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
gan: Jivkov, A, et al.
Cyhoeddwyd: (2007)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
gan: Kovac, J, et al.
Cyhoeddwyd: (2012)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
gan: Jivkov, A, et al.
Cyhoeddwyd: (2006)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
gan: Jivkov, A, et al.
Cyhoeddwyd: (2008)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
gan: Jivkov, A, et al.
Cyhoeddwyd: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
gan: Rahimi, S, et al.
Cyhoeddwyd: (2019)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
gan: King, A, et al.
Cyhoeddwyd: (2008)

Grain boundary engineering for crack bridging: A new model for intergranular stress corrosion crack (IGSCC) propagation
gan: Engelberg, D, et al.
Cyhoeddwyd: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
gan: S. Rahimi, et al.
Cyhoeddwyd: (2020-02-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
gan: P. Wriggers, et al.
Cyhoeddwyd: (2011-07-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
gan: M. Paggi, et al.
Cyhoeddwyd: (2013-04-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
gan: M. Paggi, et al.
Cyhoeddwyd: (2013-04-01)

Intergranular stresses in polycrystalline fatigue: diffraction measurement and self-consistent modelling
gan: Korsunsky, A, et al.
Cyhoeddwyd: (2003)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
gan: Rahimi, S, et al.
Cyhoeddwyd: (2008)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
gan: Rahimi, S, et al.
Cyhoeddwyd: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
gan: Rahimi, S, et al.
Cyhoeddwyd: (2009)

Intergranular stresses in polycrystalline fatigue: diffraction measurement and self-consistent modelling
gan: Korsunsky, A, et al.
Cyhoeddwyd: (2004)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
gan: Babout, L, et al.
Cyhoeddwyd: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
gan: Babout, L, et al.
Cyhoeddwyd: (2006)

Three-dimensional observation and image-based modelling of thermal strains in polycrystalline alumina
gan: Gonzalez, D, et al.
Cyhoeddwyd: (2013)

Cracks in refractory concrete: Transgranular or intergranular?
gan: Christian Jung, et al.
Cyhoeddwyd: (2025-02-01)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
gan: Janaszewski, M, et al.
Cyhoeddwyd: (2007)

Towards modelling intergranular stress-corrosion cracks using experimentally obtained grain topologies
gan: Simonovski, I, et al.
Cyhoeddwyd: (2010)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
gan: Rahimi, S, et al.
Cyhoeddwyd: (2016)