Three-dimensional characterization of stress corrosion cracks

Three-dimensional characterization of stress corrosion cracks

अन्य संस्करण दिखाएं (1)

Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome th...

पूर्ण विवरण

ग्रंथसूची विवरण
मुख्य लेखकों:	Lozano-Perez, S, Rodrigo, P, Gontard, L
स्वरूप:	Journal article
भाषा:	English
प्रकाशित:	2011

समान संसाधन

Three-dimensional characterization of stress corrosion cracks
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2011)

Understanding stress corrosion cracking with electron tomography
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2008)

Novel characterization of stress corrosion cracks
द्वारा: Lozano-Perez, S
प्रकाशित: (2008)

Novel characterization of stress corrosion cracks
द्वारा: Lozano-Perez, S
प्रकाशित: (2008)

TEM characterization of stress corrosion cracks in 304SS
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2004)

TEM characterization of stress corrosion cracks in 304SS
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2004)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
द्वारा: Jivkov, A, और अन्य
प्रकाशित: (2007)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
द्वारा: Marrow, T, और अन्य
प्रकाशित: (2006)

A multi-scale approach to stress corrosion cracking
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2008)

A multi-scale approach to stress corrosion cracking
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2008)

A study on the diffusion-induced grain boundary migration ahead of stress corrosion cracking crack tips through advanced characterization
द्वारा: Shen, Z, और अन्य
प्रकाशित: (2021)

Characterization Of Strain Hardening Three Dimensional Crack-Tip Stress Field
द्वारा: Zakaria, Muhammad Naim
प्रकाशित: (2022)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
द्वारा: Kruska, K, और अन्य
प्रकाशित: (2011)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
द्वारा: Kruska, K, और अन्य
प्रकाशित: (2011)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
द्वारा: Huang, Y, और अन्य
प्रकाशित: (2001)

Characterization of Corrosion and Stress Corrosion Cracking of AE44 Magnesium Alloy
द्वारा: M. Sozańska, और अन्य
प्रकाशित: (2020-03-01)

Stress-corrosion cracking /
द्वारा: Jones, Russell H.
प्रकाशित: (1992)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2003)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2009)

Stress corrosion cracking of pipelines /
द्वारा: Cheng, Y. Frank, 1969-
प्रकाशित: (2013)

Stress corrosion cracking of steels/
द्वारा: 287285 Karpenko, G. V., और अन्य
प्रकाशित: (1979)

Atom probe tomography of stress corrosion crack tips in SUS316 stainless steels
द्वारा: Meisnar, M, और अन्य
प्रकाशित: (2015)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
द्वारा: Jivkov, A, और अन्य
प्रकाशित: (2006)

Crack Growth Rate Analysis of Stress Corrosion Cracking
द्वारा: Mohamed Alkateb, और अन्य
प्रकाशित: (2021-01-01)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis.
द्वारा: Lozano-Perez, S
प्रकाशित: (2008)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis
द्वारा: Lozano-Perez, S
प्रकाशित: (2008)

Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB
द्वारा: Lozano-Perez, S, और अन्य
प्रकाशित: (2001)

Characterization of elastic strain field and geometrically necessary dislocation distribution in stress corrosion cracking of 316 stainless steels by transmission Kikuchi diffraction
द्वारा: Wilkinson, A, और अन्य
प्रकाशित: (2015)

Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2
द्वारा: Thuc Hue Ly, और अन्य
प्रकाशित: (2017-01-01)

Three-Dimensional Elastic-Plastic Crack Tip Stress Fields
द्वारा: Mohd Nor Halimuddin, Normalyana
प्रकाशित: (2022)

Stress corrosion cracking : theory and practice /
द्वारा: Raja, V. S., और अन्य
प्रकाशित: (2011)

Micromechanical testing of stress corrosion cracking
द्वारा: Herbert, F, और अन्य
प्रकाशित: (2010)

Understanding the mechanisms of stress corrosion cracking
द्वारा: Kruska, K
प्रकाशित: (2012)

COMPOSITION, MICROSTRUCTURE, AND STRESS-CORROSION CRACKING
द्वारा: Sykes, J
प्रकाशित: (1993)

Stress corrosion cracking test methods /
द्वारा: Sedriks, A. John, author, और अन्य
प्रकाशित: (1990)

Stress corrosion cracking of aluminium alloys /
द्वारा: 333484 Jainal Bonandar
प्रकाशित: (1986)

Stress-corrosion cracking and hydrogen embrittlement
द्वारा: British Ship Research Association
प्रकाशित: ([n d)