Three-dimensional characterization of stress corrosion cracks

Three-dimensional characterization of stress corrosion cracks

Toon andere (1) versies

Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome th...

Volledige beschrijving

Bibliografische gegevens
Hoofdauteurs:	Lozano-Perez, S, Rodrigo, P, Gontard, L
Formaat:	Journal article
Taal:	English
Gepubliceerd in:	2011

Gelijkaardige items

Three-dimensional characterization of stress corrosion cracks
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2011)

Understanding stress corrosion cracking with electron tomography
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2008)

Novel characterization of stress corrosion cracks
door: Lozano-Perez, S
Gepubliceerd in: (2008)

Novel characterization of stress corrosion cracks
door: Lozano-Perez, S
Gepubliceerd in: (2008)

TEM characterization of stress corrosion cracks in 304SS
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2004)

TEM characterization of stress corrosion cracks in 304SS
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2004)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
door: Jivkov, A, et al.
Gepubliceerd in: (2007)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
door: Marrow, T, et al.
Gepubliceerd in: (2006)

A multi-scale approach to stress corrosion cracking
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2008)

A multi-scale approach to stress corrosion cracking
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2008)

A study on the diffusion-induced grain boundary migration ahead of stress corrosion cracking crack tips through advanced characterization
door: Shen, Z, et al.
Gepubliceerd in: (2021)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
door: Kruska, K, et al.
Gepubliceerd in: (2011)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
door: Kruska, K, et al.
Gepubliceerd in: (2011)

Characterization Of Strain Hardening Three Dimensional Crack-Tip Stress Field
door: Zakaria, Muhammad Naim
Gepubliceerd in: (2022)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
door: Huang, Y, et al.
Gepubliceerd in: (2001)

Characterization of Corrosion and Stress Corrosion Cracking of AE44 Magnesium Alloy
door: M. Sozańska, et al.
Gepubliceerd in: (2020-03-01)

Stress-corrosion cracking /
door: Jones, Russell H.
Gepubliceerd in: (1992)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2003)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2009)

Stress corrosion cracking of pipelines /
door: Cheng, Y. Frank, 1969-
Gepubliceerd in: (2013)

Stress corrosion cracking of steels/
door: 287285 Karpenko, G. V., et al.
Gepubliceerd in: (1979)

Atom probe tomography of stress corrosion crack tips in SUS316 stainless steels
door: Meisnar, M, et al.
Gepubliceerd in: (2015)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
door: Jivkov, A, et al.
Gepubliceerd in: (2006)

Crack Growth Rate Analysis of Stress Corrosion Cracking
door: Mohamed Alkateb, et al.
Gepubliceerd in: (2021-01-01)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis.
door: Lozano-Perez, S
Gepubliceerd in: (2008)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis
door: Lozano-Perez, S
Gepubliceerd in: (2008)

Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB
door: Lozano-Perez, S, et al.
Gepubliceerd in: (2001)

Characterization of elastic strain field and geometrically necessary dislocation distribution in stress corrosion cracking of 316 stainless steels by transmission Kikuchi diffraction
door: Wilkinson, A, et al.
Gepubliceerd in: (2015)

Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2
door: Thuc Hue Ly, et al.
Gepubliceerd in: (2017-01-01)

Stress corrosion cracking : theory and practice /
door: Raja, V. S., et al.
Gepubliceerd in: (2011)

Micromechanical testing of stress corrosion cracking
door: Herbert, F, et al.
Gepubliceerd in: (2010)

Understanding the mechanisms of stress corrosion cracking
door: Kruska, K
Gepubliceerd in: (2012)

Three-Dimensional Elastic-Plastic Crack Tip Stress Fields
door: Mohd Nor Halimuddin, Normalyana
Gepubliceerd in: (2022)

COMPOSITION, MICROSTRUCTURE, AND STRESS-CORROSION CRACKING
door: Sykes, J
Gepubliceerd in: (1993)

Stress corrosion cracking test methods /
door: Sedriks, A. John, author, et al.
Gepubliceerd in: (1990)

Stress corrosion cracking of aluminium alloys /
door: 333484 Jainal Bonandar
Gepubliceerd in: (1986)

Stress-corrosion cracking and hydrogen embrittlement
door: British Ship Research Association
Gepubliceerd in: ([n d)