Three-dimensional characterization of stress corrosion cracks

Three-dimensional characterization of stress corrosion cracks

Показать другие версии (1)

Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome th...

Полное описание

Библиографические подробности
Главные авторы:	Lozano-Perez, S, Rodrigo, P, Gontard, L
Формат:	Journal article
Язык:	English
Опубликовано:	2011

Схожие документы

Three-dimensional characterization of stress corrosion cracks
по: Lozano-Perez, S, и др.
Опубликовано: (2011)

Understanding stress corrosion cracking with electron tomography
по: Lozano-Perez, S, и др.
Опубликовано: (2008)

Novel characterization of stress corrosion cracks
по: Lozano-Perez, S
Опубликовано: (2008)

Novel characterization of stress corrosion cracks
по: Lozano-Perez, S
Опубликовано: (2008)

TEM characterization of stress corrosion cracks in 304SS
по: Lozano-Perez, S, и др.
Опубликовано: (2004)

TEM characterization of stress corrosion cracks in 304SS
по: Lozano-Perez, S, и др.
Опубликовано: (2004)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
по: Jivkov, A, и др.
Опубликовано: (2007)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
по: Marrow, T, и др.
Опубликовано: (2006)

A multi-scale approach to stress corrosion cracking
по: Lozano-Perez, S, и др.
Опубликовано: (2008)

A multi-scale approach to stress corrosion cracking
по: Lozano-Perez, S, и др.
Опубликовано: (2008)

A study on the diffusion-induced grain boundary migration ahead of stress corrosion cracking crack tips through advanced characterization
по: Shen, Z, и др.
Опубликовано: (2021)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
по: Kruska, K, и др.
Опубликовано: (2011)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
по: Kruska, K, и др.
Опубликовано: (2011)

Characterization Of Strain Hardening Three Dimensional Crack-Tip Stress Field
по: Zakaria, Muhammad Naim
Опубликовано: (2022)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
по: Huang, Y, и др.
Опубликовано: (2001)

Characterization of Corrosion and Stress Corrosion Cracking of AE44 Magnesium Alloy
по: M. Sozańska, и др.
Опубликовано: (2020-03-01)

Stress-corrosion cracking /
по: Jones, Russell H.
Опубликовано: (1992)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
по: Lozano-Perez, S, и др.
Опубликовано: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
по: Lozano-Perez, S, и др.
Опубликовано: (2003)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
по: Lozano-Perez, S, и др.
Опубликовано: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
по: Lozano-Perez, S, и др.
Опубликовано: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
по: Lozano-Perez, S, и др.
Опубликовано: (2009)

Stress corrosion cracking of pipelines /
по: Cheng, Y. Frank, 1969-
Опубликовано: (2013)

Stress corrosion cracking of steels/
по: 287285 Karpenko, G. V., и др.
Опубликовано: (1979)

Atom probe tomography of stress corrosion crack tips in SUS316 stainless steels
по: Meisnar, M, и др.
Опубликовано: (2015)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
по: Jivkov, A, и др.
Опубликовано: (2006)

Crack Growth Rate Analysis of Stress Corrosion Cracking
по: Mohamed Alkateb, и др.
Опубликовано: (2021-01-01)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis.
по: Lozano-Perez, S
Опубликовано: (2008)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis
по: Lozano-Perez, S
Опубликовано: (2008)

Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB
по: Lozano-Perez, S, и др.
Опубликовано: (2001)

Characterization of elastic strain field and geometrically necessary dislocation distribution in stress corrosion cracking of 316 stainless steels by transmission Kikuchi diffraction
по: Wilkinson, A, и др.
Опубликовано: (2015)

Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2
по: Thuc Hue Ly, и др.
Опубликовано: (2017-01-01)

Stress corrosion cracking : theory and practice /
по: Raja, V. S., и др.
Опубликовано: (2011)

Micromechanical testing of stress corrosion cracking
по: Herbert, F, и др.
Опубликовано: (2010)

Understanding the mechanisms of stress corrosion cracking
по: Kruska, K
Опубликовано: (2012)

Three-Dimensional Elastic-Plastic Crack Tip Stress Fields
по: Mohd Nor Halimuddin, Normalyana
Опубликовано: (2022)

COMPOSITION, MICROSTRUCTURE, AND STRESS-CORROSION CRACKING
по: Sykes, J
Опубликовано: (1993)

Stress corrosion cracking test methods /
по: Sedriks, A. John, author, и др.
Опубликовано: (1990)

Stress corrosion cracking of aluminium alloys /
по: 333484 Jainal Bonandar
Опубликовано: (1986)

Stress-corrosion cracking and hydrogen embrittlement
по: British Ship Research Association
Опубликовано: ([n d)