Three-dimensional characterization of stress corrosion cracks

Three-dimensional characterization of stress corrosion cracks

Hiển thị phiên bản (1) khác

Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome th...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Lozano-Perez, S, Rodrigo, P, Gontard, L
Định dạng:	Journal article
Ngôn ngữ:	English
Được phát hành:	2011

Những quyển sách tương tự

Three-dimensional characterization of stress corrosion cracks
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2011)

Understanding stress corrosion cracking with electron tomography
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2008)

Novel characterization of stress corrosion cracks
Bằng: Lozano-Perez, S
Được phát hành: (2008)

Novel characterization of stress corrosion cracks
Bằng: Lozano-Perez, S
Được phát hành: (2008)

TEM characterization of stress corrosion cracks in 304SS
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2004)

TEM characterization of stress corrosion cracks in 304SS
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2004)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
Bằng: Jivkov, A, et al.
Được phát hành: (2007)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
Bằng: Marrow, T, et al.
Được phát hành: (2006)

A multi-scale approach to stress corrosion cracking
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2008)

A multi-scale approach to stress corrosion cracking
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2008)

A study on the diffusion-induced grain boundary migration ahead of stress corrosion cracking crack tips through advanced characterization
Bằng: Shen, Z, et al.
Được phát hành: (2021)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
Bằng: Kruska, K, et al.
Được phát hành: (2011)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
Bằng: Kruska, K, et al.
Được phát hành: (2011)

Characterization Of Strain Hardening Three Dimensional Crack-Tip Stress Field
Bằng: Zakaria, Muhammad Naim
Được phát hành: (2022)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
Bằng: Huang, Y, et al.
Được phát hành: (2001)

Characterization of Corrosion and Stress Corrosion Cracking of AE44 Magnesium Alloy
Bằng: M. Sozańska, et al.
Được phát hành: (2020-03-01)

Stress-corrosion cracking /
Bằng: Jones, Russell H.
Được phát hành: (1992)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2003)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2009)

Stress corrosion cracking of pipelines /
Bằng: Cheng, Y. Frank, 1969-
Được phát hành: (2013)

Stress corrosion cracking of steels/
Bằng: 287285 Karpenko, G. V., et al.
Được phát hành: (1979)

Atom probe tomography of stress corrosion crack tips in SUS316 stainless steels
Bằng: Meisnar, M, et al.
Được phát hành: (2015)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
Bằng: Jivkov, A, et al.
Được phát hành: (2006)

Crack Growth Rate Analysis of Stress Corrosion Cracking
Bằng: Mohamed Alkateb, et al.
Được phát hành: (2021-01-01)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis.
Bằng: Lozano-Perez, S
Được phát hành: (2008)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis
Bằng: Lozano-Perez, S
Được phát hành: (2008)

Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB
Bằng: Lozano-Perez, S, et al.
Được phát hành: (2001)

Characterization of elastic strain field and geometrically necessary dislocation distribution in stress corrosion cracking of 316 stainless steels by transmission Kikuchi diffraction
Bằng: Wilkinson, A, et al.
Được phát hành: (2015)

Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2
Bằng: Thuc Hue Ly, et al.
Được phát hành: (2017-01-01)

Stress corrosion cracking : theory and practice /
Bằng: Raja, V. S., et al.
Được phát hành: (2011)

Micromechanical testing of stress corrosion cracking
Bằng: Herbert, F, et al.
Được phát hành: (2010)

Understanding the mechanisms of stress corrosion cracking
Bằng: Kruska, K
Được phát hành: (2012)

Three-Dimensional Elastic-Plastic Crack Tip Stress Fields
Bằng: Mohd Nor Halimuddin, Normalyana
Được phát hành: (2022)

COMPOSITION, MICROSTRUCTURE, AND STRESS-CORROSION CRACKING
Bằng: Sykes, J
Được phát hành: (1993)

Stress corrosion cracking test methods /
Bằng: Sedriks, A. John, author, et al.
Được phát hành: (1990)

Stress corrosion cracking of aluminium alloys /
Bằng: 333484 Jainal Bonandar
Được phát hành: (1986)

Stress-corrosion cracking and hydrogen embrittlement
Bằng: British Ship Research Association
Được phát hành: ([n d)