Novel characterization of stress corrosion cracks

Novel characterization of stress corrosion cracks

Show other versions (1)

A multi-scale approach to stress corrosion cracking is presented in this paper. It will be shown that the same crack and, more importantly, the crack tip region can be characterized with surface techniques such as NanoSIMS and EBSD and later prepared for TEM or Atom Probe. This will offer a unique i...

Disgrifiad llawn

Manylion Llyfryddiaeth
Prif Awdur:	Lozano-Perez, S
Fformat:	Conference item
Cyhoeddwyd:	2008

Eitemau Tebyg

Novel characterization of stress corrosion cracks
gan: Lozano-Perez, S
Cyhoeddwyd: (2008)

Three-dimensional characterization of stress corrosion cracks
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2011)

Three-dimensional characterization of stress corrosion cracks
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2011)

TEM characterization of stress corrosion cracks in 304SS
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2004)

TEM characterization of stress corrosion cracks in 304SS
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2004)

Understanding stress corrosion cracking with electron tomography
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2008)

A multi-scale approach to stress corrosion cracking
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2008)

A multi-scale approach to stress corrosion cracking
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2008)

A study on the diffusion-induced grain boundary migration ahead of stress corrosion cracking crack tips through advanced characterization
gan: Shen, Z, et al.
Cyhoeddwyd: (2021)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
gan: Huang, Y, et al.
Cyhoeddwyd: (2001)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
gan: Kruska, K, et al.
Cyhoeddwyd: (2011)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
gan: Kruska, K, et al.
Cyhoeddwyd: (2011)

Characterization of Corrosion and Stress Corrosion Cracking of AE44 Magnesium Alloy
gan: M. Sozańska, et al.
Cyhoeddwyd: (2020-03-01)

Stress-corrosion cracking /
gan: Jones, Russell H.
Cyhoeddwyd: (1992)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2003)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2009)

Stress corrosion cracking of pipelines /
gan: Cheng, Y. Frank, 1969-
Cyhoeddwyd: (2013)

Stress corrosion cracking of steels/
gan: 287285 Karpenko, G. V., et al.
Cyhoeddwyd: (1979)

Atom probe tomography of stress corrosion crack tips in SUS316 stainless steels
gan: Meisnar, M, et al.
Cyhoeddwyd: (2015)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis
gan: Lozano-Perez, S
Cyhoeddwyd: (2008)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis.
gan: Lozano-Perez, S
Cyhoeddwyd: (2008)

Crack Growth Rate Analysis of Stress Corrosion Cracking
gan: Mohamed Alkateb, et al.
Cyhoeddwyd: (2021-01-01)

Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB
gan: Lozano-Perez, S, et al.
Cyhoeddwyd: (2001)

Characterization of elastic strain field and geometrically necessary dislocation distribution in stress corrosion cracking of 316 stainless steels by transmission Kikuchi diffraction
gan: Wilkinson, A, et al.
Cyhoeddwyd: (2015)

COMPOSITION, MICROSTRUCTURE, AND STRESS-CORROSION CRACKING
gan: Sykes, J
Cyhoeddwyd: (1993)

Micromechanical testing of stress corrosion cracking
gan: Herbert, F, et al.
Cyhoeddwyd: (2010)

Understanding the mechanisms of stress corrosion cracking
gan: Kruska, K
Cyhoeddwyd: (2012)

Stress corrosion cracking : theory and practice /
gan: Raja, V. S., et al.
Cyhoeddwyd: (2011)

Stress corrosion cracking test methods /
gan: Sedriks, A. John, author, et al.
Cyhoeddwyd: (1990)

Stress corrosion cracking of aluminium alloys /
gan: 333484 Jainal Bonandar
Cyhoeddwyd: (1986)

Stress-corrosion cracking and hydrogen embrittlement
gan: British Ship Research Association
Cyhoeddwyd: ([n d)

Stress corrosion cracking and crack tip characterization of Alloy X-750 in light water reactor environments
gan: Gibbs, Jonathan Paul
Cyhoeddwyd: (2013)

Stress Corrosion Cracking and Crack Tip Characterization of Alloy X-750 in Light Water Reactor Environments
gan: Gibbs, Jonathan Paul, et al.
Cyhoeddwyd: (2012)

Low-energy EDX - A novel approach to study stress corrosion cracking in SUS304 stainless steel via scanning electron microscopy
gan: Meisnar, M, et al.
Cyhoeddwyd: (2014)

Understanding the mechanisms controlling stress corrosion cracking through high-resolution characterization
gan: Shen, Z
Cyhoeddwyd: (2018)

On the role of intergranular carbides on improving the stress corrosion cracking resistance in a cold-worked alloy 600
gan: Shen, Z, et al.
Cyhoeddwyd: (2018)

On the role of intergranular nanocavities in long-term stress corrosion cracking of Alloy 690
gan: Shen, Z, et al.
Cyhoeddwyd: (2021)