Novel characterization of stress corrosion cracks

Novel characterization of stress corrosion cracks

Показать другие версии (1)

A multi-scale approach to stress corrosion cracking is presented in this paper. It will be shown that the same crack and, more importantly, the crack tip region can be characterized with surface techniques such as NanoSIMS and EBSD and later prepared for TEM or Atom Probe. This will offer a unique i...

Полное описание

Библиографические подробности
Главный автор:	Lozano-Perez, S
Формат:	Conference item
Опубликовано:	2008

Схожие документы

Novel characterization of stress corrosion cracks
по: Lozano-Perez, S
Опубликовано: (2008)

Three-dimensional characterization of stress corrosion cracks
по: Lozano-Perez, S, и др.
Опубликовано: (2011)

Three-dimensional characterization of stress corrosion cracks
по: Lozano-Perez, S, и др.
Опубликовано: (2011)

TEM characterization of stress corrosion cracks in 304SS
по: Lozano-Perez, S, и др.
Опубликовано: (2004)

TEM characterization of stress corrosion cracks in 304SS
по: Lozano-Perez, S, и др.
Опубликовано: (2004)

Understanding stress corrosion cracking with electron tomography
по: Lozano-Perez, S, и др.
Опубликовано: (2008)

A multi-scale approach to stress corrosion cracking
по: Lozano-Perez, S, и др.
Опубликовано: (2008)

A multi-scale approach to stress corrosion cracking
по: Lozano-Perez, S, и др.
Опубликовано: (2008)

A study on the diffusion-induced grain boundary migration ahead of stress corrosion cracking crack tips through advanced characterization
по: Shen, Z, и др.
Опубликовано: (2021)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
по: Huang, Y, и др.
Опубликовано: (2001)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
по: Kruska, K, и др.
Опубликовано: (2011)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
по: Kruska, K, и др.
Опубликовано: (2011)

Characterization of Corrosion and Stress Corrosion Cracking of AE44 Magnesium Alloy
по: M. Sozańska, и др.
Опубликовано: (2020-03-01)

Stress-corrosion cracking /
по: Jones, Russell H.
Опубликовано: (1992)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
по: Lozano-Perez, S, и др.
Опубликовано: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
по: Lozano-Perez, S, и др.
Опубликовано: (2003)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
по: Lozano-Perez, S, и др.
Опубликовано: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
по: Lozano-Perez, S, и др.
Опубликовано: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
по: Lozano-Perez, S, и др.
Опубликовано: (2009)

Stress corrosion cracking of pipelines /
по: Cheng, Y. Frank, 1969-
Опубликовано: (2013)

Stress corrosion cracking of steels/
по: 287285 Karpenko, G. V., и др.
Опубликовано: (1979)

Atom probe tomography of stress corrosion crack tips in SUS316 stainless steels
по: Meisnar, M, и др.
Опубликовано: (2015)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis
по: Lozano-Perez, S
Опубликовано: (2008)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis.
по: Lozano-Perez, S
Опубликовано: (2008)

Crack Growth Rate Analysis of Stress Corrosion Cracking
по: Mohamed Alkateb, и др.
Опубликовано: (2021-01-01)

Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB
по: Lozano-Perez, S, и др.
Опубликовано: (2001)

Characterization of elastic strain field and geometrically necessary dislocation distribution in stress corrosion cracking of 316 stainless steels by transmission Kikuchi diffraction
по: Wilkinson, A, и др.
Опубликовано: (2015)

COMPOSITION, MICROSTRUCTURE, AND STRESS-CORROSION CRACKING
по: Sykes, J
Опубликовано: (1993)

Micromechanical testing of stress corrosion cracking
по: Herbert, F, и др.
Опубликовано: (2010)

Understanding the mechanisms of stress corrosion cracking
по: Kruska, K
Опубликовано: (2012)

Stress corrosion cracking : theory and practice /
по: Raja, V. S., и др.
Опубликовано: (2011)

Stress corrosion cracking test methods /
по: Sedriks, A. John, author, и др.
Опубликовано: (1990)

Stress corrosion cracking of aluminium alloys /
по: 333484 Jainal Bonandar
Опубликовано: (1986)

Stress-corrosion cracking and hydrogen embrittlement
по: British Ship Research Association
Опубликовано: ([n d)

Stress corrosion cracking and crack tip characterization of Alloy X-750 in light water reactor environments
по: Gibbs, Jonathan Paul
Опубликовано: (2013)

Stress Corrosion Cracking and Crack Tip Characterization of Alloy X-750 in Light Water Reactor Environments
по: Gibbs, Jonathan Paul, и др.
Опубликовано: (2012)

Low-energy EDX - A novel approach to study stress corrosion cracking in SUS304 stainless steel via scanning electron microscopy
по: Meisnar, M, и др.
Опубликовано: (2014)

Understanding the mechanisms controlling stress corrosion cracking through high-resolution characterization
по: Shen, Z
Опубликовано: (2018)

On the role of intergranular carbides on improving the stress corrosion cracking resistance in a cold-worked alloy 600
по: Shen, Z, и др.
Опубликовано: (2018)

On the role of intergranular nanocavities in long-term stress corrosion cracking of Alloy 690
по: Shen, Z, и др.
Опубликовано: (2021)