Measurement of small misorientations using electron back scatter diffraction
This paper concerns the determination of small misorientations using electron back scatter diffraction (EBSD). Generally EBSD is used to measure crystal orientations from which misorientations can be calculated. Repeated measurements on undeformed Si showed that the calculated misorientations have a...
1. Verfasser: | Wilkinson, A |
---|---|
Format: | Conference item |
Veröffentlicht: |
1999
|
Ähnliche Einträge
Ähnliche Einträge
-
A new method for determining small misorientations from electron back scatter diffraction patterns
von: Wilkinson, A
Veröffentlicht: (2001) -
Strain measurement using electron back scatter diffraction
von: Wilkinson, A
Veröffentlicht: (1998) -
Measurement of elastic strains and small lattice rotations using electron back scatter diffraction.
von: Wilkinson, A
Veröffentlicht: (1996) -
Mapping strains at the nanoscale using electron back scatter diffraction
von: Wilkinson, A, et al.
Veröffentlicht: (2009) -
Strain tensor mapping at the nanoscale using electron back scatter diffraction
von: Wilkinson, A, et al.
Veröffentlicht: (2006)