Crack field analysis by optical DIC of short cracks in Zircaloy-4

Crack field analysis by optical DIC of short cracks in Zircaloy-4

The prediction of fatigue life is most difficult for short cracks, as their local conditions may differ from what is predicted using the remote applied loading and crack geometry. Digital image correlation (DIC) can be utilized to analyze images from an optical microscope (OM), which facilitates the...

Descripció completa

Dades bibliogràfiques
Autors principals:	Su, X, Wan, W, Dunne, FPE, Marrow, TJ
Format:	Conference item
Idioma:	English
Publicat:	Elsevier 2022

Ítems similars

J-integral analysis: an EDXD and DIC comparative study for a fatigue crack
per: Koko, A, et al.
Publicat: (2020)

Stress corrosion cracking of Zircaloy in the prescence of iodine
per: Knorr, David Bruce
Publicat: (2005)

Stress Corrosion Cracking of Zircaloy-4 in Halide Solutions: Effect of Temperature
per: Farina S.B., et al.
Publicat: (2002-01-01)

An FFT-based crystal plasticity phase-field model for micromechanical fatigue cracking based on the stored energy density
per: Lucarini, S, et al.
Publicat: (2023)

Approximation of the crack-tip field in fatigue cracks in bridge steel specimens: DIC analysis of different constraint levels
per: Stanislav Seitl, et al.
Publicat: (2019-06-01)

Approximation of the crack-tip field in fatigue cracks in bridge steel specimens: DIC analysis of different constraint levels
per: S. Seitl, et al.
Publicat: (2019-07-01)

3D focused ion beam sectioning of zirconium oxides in Zircaloy-4 for the characterisation of cracking
per: Weekes, HE, et al.
Publicat: (2020)

Interfacial Cracking Failure Mechanism of Chromium-Coated Zircaloy Cladding for ATF Materials
per: Xinfeng Li, et al.
Publicat: (2025-02-01)

Effect of initial coating crack on the mechanical performance of surface-coated zircaloy cladding
per: Ze Xu, et al.
Publicat: (2021-04-01)

Experimental characterisation of fatigue crack growth based on the CTOD measured from crack tip displacement fields using DIC
per: José Manuel Vasco Olmo, et al.
Publicat: (2019-09-01)

Experimental characterisation of fatigue crack growth based on the CTOD measured from crack tip displacement fields using DIC
per: J.M. Vasco-Olmo, et al.
Publicat: (2019-10-01)

LCF and crack growth: recent results obtained by DIC
per: Patriarca Luca, et al.
Publicat: (2018-01-01)

Three-dimensional numerical simulation of hydrogen-induced multi-field coupling behavior in cracked zircaloy cladding tubes
per: Zhongjia Xia, et al.
Publicat: (2019-02-01)

Characterization of Bonded Zone and Evaluation of Cracking in Vacuum Brazed Zircaloy-4 and Stainless Steel-316L Joint
per: A. Munis, et al.
Publicat: (2019-06-01)

3-Dimensional analysis of fatigue crack fields and crack growth by in situ synchrotron X-ray tomography
per: Koko, A, et al.
Publicat: (2023)

Assessment of the fracture toughness of neutron-irradiated nuclear graphite by 3D analysis of the crack displacement field
per: Jin, X, et al.
Publicat: (2020)

Got it cracked?
per: Marrow, J
Publicat: (2009)

Short fatigue cracks in austempered ductile cast iron (ADI)
per: Marrow, T, et al.
Publicat: (2000)

Improvement of crack tip position estimation in DIC images by image processing methods
per: Zekriti Najat, et al.
Publicat: (2023-01-01)

Improvement of crack tip position estimation in DIC images by image processing methods
per: Najat Zekriti, et al.
Publicat: (2022-12-01)

Stress relaxation of Zircaloy-4.
per: Minar, Arthur Phillip
Publicat: (2013)

Mechanism of the HIP bonding of Zircaloy-4 in the alpha-phase field
per: Hill, P, et al.
Publicat: (2003)

Study on crack propagation characteristics of rocks with different lateral pressure based on joint monitoring of DIC and AE
per: Wei Zhang, et al.
Publicat: (2024-08-01)

Influence of Twins on Short Fatigue Cracks in Type 316L Stainless Steel
per: Al-Shahrani, S, et al.
Publicat: (2011)

Application of Digital Image Correlation (DIC) in resonance machines for measuring fatigue crack growth
per: P. Lorenzino, et al.
Publicat: (2014-09-01)

Application of Digital Image Correlation (DIC) in resonance machines for measuring fatigue crack growth
per: P. Lorenzino, et al.
Publicat: (2014-10-01)

Crack Propagation Phenomenon in Gangue Concrete Using the Digital Image Correlation (DIC) Method
per: Cheng Pan, et al.
Publicat: (2024-01-01)

Study on Crack Propagation and Coalescence in Fractured Limestone Based on 3D-DIC Technology
per: Yanyan Peng, et al.
Publicat: (2022-03-01)

A novel DIC-based methodology for crack identification in a jointed rock mass
per: Ke Zhang, et al.
Publicat: (2023-06-01)

Experimental study on crack propagation pattern and fracture process zone evolution based on far-field displacement by using DIC
per: Yang Qiao, et al.
Publicat: (2023-11-01)

Controlled initiation of short fatigue cracks in 316L steel
per: Stefanescu, D, et al.
Publicat: (2005)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
per: S. Rahimi, et al.
Publicat: (2020-02-01)

In situ observation of short fatigue crack propagation in oxygenated water at elevated temperature and pressure
per: Duff, J, et al.
Publicat: (2013)

In situ observation of short fatigue crack propagation in oxygenated water at elevated temperature and pressure
per: Duff, J, et al.
Publicat: (2013)

Quantitative in situ study of short crack propagation in polygranular graphite by digital image correlation
per: Mostafavi, M, et al.
Publicat: (2012)

Quantitative in situ study of short crack propagation in polygranular graphite by digital image correlation
per: Mostafavi, M, et al.
Publicat: (2012)

Strength Characteristics and Failure Mechanism of Granite with Cross Cracks at Different Angles Based on DIC Method
per: Xu Wu, et al.
Publicat: (2022-01-01)

Study on the evolution process of drying-wetting cycle cracks in compacted loess based on DIC technology
per: Hu Changming, et al.
Publicat: (2023-01-01)

Three-dimensional in situ observations of short fatigue crack growth in magnesium
per: King, A, et al.
Publicat: (2011)

HR-EBSD analysis of in situ stable crack growth at the micron scale
per: Koko, A, et al.
Publicat: (2022)