Crack field analysis by optical DIC of short cracks in Zircaloy-4

Crack field analysis by optical DIC of short cracks in Zircaloy-4

The prediction of fatigue life is most difficult for short cracks, as their local conditions may differ from what is predicted using the remote applied loading and crack geometry. Digital image correlation (DIC) can be utilized to analyze images from an optical microscope (OM), which facilitates the...

書目詳細資料
Main Authors:	Su, X, Wan, W, Dunne, FPE, Marrow, TJ
格式:	Conference item
語言:	English
出版:	Elsevier 2022

相似書籍

J-integral analysis: an EDXD and DIC comparative study for a fatigue crack
由: Koko, A, et al.
出版: (2020)

Stress corrosion cracking of Zircaloy in the prescence of iodine
由: Knorr, David Bruce
出版: (2005)

Stress Corrosion Cracking of Zircaloy-4 in Halide Solutions: Effect of Temperature
由: Farina S.B., et al.
出版: (2002-01-01)

An FFT-based crystal plasticity phase-field model for micromechanical fatigue cracking based on the stored energy density
由: Lucarini, S, et al.
出版: (2023)

Approximation of the crack-tip field in fatigue cracks in bridge steel specimens: DIC analysis of different constraint levels
由: Stanislav Seitl, et al.
出版: (2019-06-01)

Approximation of the crack-tip field in fatigue cracks in bridge steel specimens: DIC analysis of different constraint levels
由: S. Seitl, et al.
出版: (2019-07-01)

3D focused ion beam sectioning of zirconium oxides in Zircaloy-4 for the characterisation of cracking
由: Weekes, HE, et al.
出版: (2020)

Interfacial Cracking Failure Mechanism of Chromium-Coated Zircaloy Cladding for ATF Materials
由: Xinfeng Li, et al.
出版: (2025-02-01)

Effect of initial coating crack on the mechanical performance of surface-coated zircaloy cladding
由: Ze Xu, et al.
出版: (2021-04-01)

Experimental characterisation of fatigue crack growth based on the CTOD measured from crack tip displacement fields using DIC
由: José Manuel Vasco Olmo, et al.
出版: (2019-09-01)

Experimental characterisation of fatigue crack growth based on the CTOD measured from crack tip displacement fields using DIC
由: J.M. Vasco-Olmo, et al.
出版: (2019-10-01)

LCF and crack growth: recent results obtained by DIC
由: Patriarca Luca, et al.
出版: (2018-01-01)

Three-dimensional numerical simulation of hydrogen-induced multi-field coupling behavior in cracked zircaloy cladding tubes
由: Zhongjia Xia, et al.
出版: (2019-02-01)

Characterization of Bonded Zone and Evaluation of Cracking in Vacuum Brazed Zircaloy-4 and Stainless Steel-316L Joint
由: A. Munis, et al.
出版: (2019-06-01)

3-Dimensional analysis of fatigue crack fields and crack growth by in situ synchrotron X-ray tomography
由: Koko, A, et al.
出版: (2023)

Assessment of the fracture toughness of neutron-irradiated nuclear graphite by 3D analysis of the crack displacement field
由: Jin, X, et al.
出版: (2020)

Got it cracked?
由: Marrow, J
出版: (2009)

Short fatigue cracks in austempered ductile cast iron (ADI)
由: Marrow, T, et al.
出版: (2000)

Improvement of crack tip position estimation in DIC images by image processing methods
由: Zekriti Najat, et al.
出版: (2023-01-01)

Improvement of crack tip position estimation in DIC images by image processing methods
由: Najat Zekriti, et al.
出版: (2022-12-01)

Stress relaxation of Zircaloy-4.
由: Minar, Arthur Phillip
出版: (2013)

Mechanism of the HIP bonding of Zircaloy-4 in the alpha-phase field
由: Hill, P, et al.
出版: (2003)

Study on crack propagation characteristics of rocks with different lateral pressure based on joint monitoring of DIC and AE
由: Wei Zhang, et al.
出版: (2024-08-01)

Influence of Twins on Short Fatigue Cracks in Type 316L Stainless Steel
由: Al-Shahrani, S, et al.
出版: (2011)

Application of Digital Image Correlation (DIC) in resonance machines for measuring fatigue crack growth
由: P. Lorenzino, et al.
出版: (2014-09-01)

Application of Digital Image Correlation (DIC) in resonance machines for measuring fatigue crack growth
由: P. Lorenzino, et al.
出版: (2014-10-01)

Crack Propagation Phenomenon in Gangue Concrete Using the Digital Image Correlation (DIC) Method
由: Cheng Pan, et al.
出版: (2024-01-01)

Study on Crack Propagation and Coalescence in Fractured Limestone Based on 3D-DIC Technology
由: Yanyan Peng, et al.
出版: (2022-03-01)

A novel DIC-based methodology for crack identification in a jointed rock mass
由: Ke Zhang, et al.
出版: (2023-06-01)

Experimental study on crack propagation pattern and fracture process zone evolution based on far-field displacement by using DIC
由: Yang Qiao, et al.
出版: (2023-11-01)

Controlled initiation of short fatigue cracks in 316L steel
由: Stefanescu, D, et al.
出版: (2005)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
由: S. Rahimi, et al.
出版: (2020-02-01)

In situ observation of short fatigue crack propagation in oxygenated water at elevated temperature and pressure
由: Duff, J, et al.
出版: (2013)

In situ observation of short fatigue crack propagation in oxygenated water at elevated temperature and pressure
由: Duff, J, et al.
出版: (2013)

Quantitative in situ study of short crack propagation in polygranular graphite by digital image correlation
由: Mostafavi, M, et al.
出版: (2012)

Quantitative in situ study of short crack propagation in polygranular graphite by digital image correlation
由: Mostafavi, M, et al.
出版: (2012)

Strength Characteristics and Failure Mechanism of Granite with Cross Cracks at Different Angles Based on DIC Method
由: Xu Wu, et al.
出版: (2022-01-01)

Study on the evolution process of drying-wetting cycle cracks in compacted loess based on DIC technology
由: Hu Changming, et al.
出版: (2023-01-01)

Three-dimensional in situ observations of short fatigue crack growth in magnesium
由: King, A, et al.
出版: (2011)

HR-EBSD analysis of in situ stable crack growth at the micron scale
由: Koko, A, et al.
出版: (2022)