Work of indentation approach to the analysis of hardness and modulus of thin coatings

Work of indentation approach to the analysis of hardness and modulus of thin coatings

Hiển thị phiên bản (1) khác

The problem of accurate identification of mechanical properties, primarily hardness and modulus, invariably arises whenever very thin coatings are considered that consist of single or multiple layers, e.g. in the context of fitness-for-purpose characterisation of coated systems, monitoring in-servic...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Korsunsky, A, Constantinescu, A
Định dạng:	Journal article
Ngôn ngữ:	English
Được phát hành:	Elsevier 2006
Những chủ đề:	Engineering & allied sciences

Những quyển sách tương tự

Indentation hardness evaluation of cathodic arc deposited thin hard coatings
Bằng: Tuck, J, et al.
Được phát hành: (2001)

The influence of indenter bluntness on the apparent contact stiffness of thin coatings
Bằng: Korsunsky, A, et al.
Được phát hành: (2009)

On property deconvolution from indentation of coated systems
Bằng: Korsunsky, A, et al.
Được phát hành: (2015)

On the application of the work-of-indentation appproach to depth-sensing indentation experiments in coated systems
Bằng: Tuck, J, et al.
Được phát hành: (2001)

Work of indentation approach to the analysis of hardness and modulus of thin coatings
Bằng: Korsunsky, A, et al.
Được phát hành: (2006)

On the hardness of coated systems
Bằng: Korsunsky, A, et al.
Được phát hành: (1998)

The influence of coating cracking and debonding on the hardness of coated systems
Bằng: Tuck, J, et al.
Được phát hành: (2000)

The influence of punch blunting on the elastic indentation response
Bằng: Korsunsky, A
Được phát hành: (2001)

Modelling of the hardness of electroplated nickel coatings on copper substrates
Bằng: Tuck, J, et al.
Được phát hành: (2000)

Mechanical properties of thin carbon overcoats
Bằng: Bull, S, et al.
Được phát hành: (1998)

Fundamental formulation for frictional contact problems of coated systems
Bằng: Ma, L, et al.
Được phát hành: (2004)

Contact of coated systems under sliding conditions
Bằng: Ma, L, et al.
Được phát hành: (2006)

A new mechanochemical method for metal coating
Bằng: Torosyan, A, et al.
Được phát hành: (2002)

Dissipated energy and fretting damage in CoCrAlY-MoS₂ coatings
Bằng: Kim, K, et al.
Được phát hành: (2010)

Exponential evolution law of fretting wear damage in low-friction coatings for aerospace components
Bằng: Kim, K, et al.
Được phát hành: (2008)

Dissipated energy and friction coefficient evolution during fretting wear of solid lubricant coatings
Bằng: Korsunsky, A, et al.
Được phát hành: (2009)

Analysis of essential work of rupture using non-local damage-plasticity modelling
Bằng: Korsunsky, A, et al.
Được phát hành: (2005)

Development and characterization of low friction coatings for protection against fretting wear in aerospace components
Bằng: Korsunsky, A, et al.
Được phát hành: (2008)

The analysis of deformation size effects using multiple gauge length extensometry and the essential work of rupture concept
Bằng: Korsunsky, A, et al.
Được phát hành: (2006)

Determination of essential work of necking and tearing from a single tensile test
Bằng: Korsunsky, A, et al.
Được phát hành: (2005)

An analysis of residual stresses and strains in shot peening
Bằng: Korsunsky, A
Được phát hành: (1997)

Development of an approach to constitutive modelling of concrete: isotropic damage coupled with plasticity
Bằng: Nguyen, G, et al.
Được phát hành: (2008)

Residual elastic strains in autofrettaged tubes: elastic-ideally plastic model analysis
Bằng: Korsunsky, A
Được phát hành: (2007)

Indentation hardness evaluation of cathodic are deposited thin hard coatings
Bằng: Tuck, JR, et al.
Được phát hành: (2001)

Variational eigenstrain analysis of synchrotron diffraction measurements of residual elastic strain in a bent titanium alloy bar
Bằng: Korsunsky, A
Được phát hành: (2006)

Engineering at large scale: Experience from diamond light source
Bằng: Korsunsky, A, et al.
Được phát hành: (2010)

Residual stresses induced by foreign object damage on gas tubine blades: an experimental approach
Bằng: Duo, P, et al.
Được phát hành: (2015)

Advanced strain analysis by high energy synchrotron X-ray diffraction
Bằng: Korsunsky, A, et al.
Được phát hành: (2002)

Vector J-integral analysis of crack initiation at the edge of complete sliding contact
Bằng: Ma, L, et al.
Được phát hành: (2006)

Analysis of cohesive zones in cracks and slip bands using hypersingular interpolative quadratures
Bằng: Korsunsky, A, et al.
Được phát hành: (2000)

An analysis of defect size evolution
Bằng: Korsunsky, A, et al.
Được phát hành: (2004)

Vector J-integral analysis of crack interaction with pre-existing singularities
Bằng: Ma, L, et al.
Được phát hành: (2006)

Microstructure, residual strain, and eigenstrain analysis of dissimilar friction stir welds
Bằng: Jun, T, et al.
Được phát hành: (2010)

Strain gradient polycrystal plasticity analysis: Fe modeling and synchrotron X-ray diffraction
Bằng: Song, X, et al.
Được phát hành: (2010)

Analysis of residual stresses around 'dimpled' cold-expanded holes in aluminum alloy plates
Bằng: Zhang, S, et al.
Được phát hành: (2008)

Analysis of residual stresses around welds in a combustion casing
Bằng: Song, X, et al.
Được phát hành: (2009)

Variational eigenstrain analysis of residual stresses in a welded plate
Bằng: Korsunsky, A, et al.
Được phát hành: (2007)

Residual elastic strain due to laser shock peening: modelling by eigenstrain distribution
Bằng: Korsunsky, A
Được phát hành: (2006)

On the size effects and scale transitions in the strength and failure of materials and structures
Bằng: Korsunsky, A
Được phát hành: (2009)

The Somigliana ring dislocation revisited: 1. Papkovich potential solutions for dislocations in an infinite space
Bằng: Korsunsky, A
Được phát hành: (1996)