$Indentation fracture toughness and surface flaw analysis of sintered alumina/SiC nanocomposites$

Indentation fracture toughness and surface flaw analysis of sintered alumina/SiC nanocomposites

The fracture toughness (K1c) of pressureless-sintered monolithic α-alumina and its composites with 5, 10 and 15 vol% SiC nano-sized particles was investigated using Vickers indentation and a new Hertzian (ball) indentation technique. Both methods showed that the fracture toughness of the composites...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Anya, C, Roberts, S
Định dạng:	Journal article
Được phát hành:	1996

Những quyển sách tương tự

Wet erosion behaviour of low SiC alumina-SiC nanocomposites
Bằng: Kara, H, et al.
Được phát hành: (2002)

Study and Analysis of Al2O3-SiC Nanocomposite Ceramics’ Fracture Toughness using Vickers Indenter
Bằng: AliReza Moradkhani, et al.
Được phát hành: (2011-06-01)

Pressureless sintering and elastic constants of Al2O3-SiC 'nanocomposites'
Bằng: Anya, C, et al.
Được phát hành: (1997)

Fracture toughness measurements of LPS-SiC: a comparison of the indentation technique and the SEVNB method
Bằng: Kurt Strecker, et al.
Được phát hành: (2005-06-01)

Erosive wear of alumina/SiC nanocomposite ceramics
Bằng: Lawrence, C, et al.
Được phát hành: (1999)

Thermal shock resistance of sintered alumina/silicon carbide nanocomposites evaluated by indentation techniques
Bằng: Maensiri, S, et al.
Được phát hành: (2002)

Crack deflection and interfacial fracture energies in alumina/SiC and alumina/TiN nanocomposites
Bằng: Jiao, S, et al.
Được phát hành: (1997)

Fracture toughness, surface flaw sizes and flaw densities in Al2O3
Bằng: Franco, A, et al.
Được phát hành: (1997)

An indentation model for erosive wear in Al2O3/SiC nanocomposites
Bằng: Shapiro, I, et al.
Được phát hành: (2011)

Dynamic Fracture Toughness of TaC/CNTs/SiC CMCs Prepared by Spark Plasma Sintering
Bằng: Qiaoyun Xie, et al.
Được phát hành: (2015-01-01)

INSTRUMENTED INDENTATION OF Al2O3-SiC NANOCOMPOSITES
Bằng: Csehova, E, et al.
Được phát hành: (2011)

Quantitative surface fractography of alumina and alumina-SiC composites during diamond grinding
Bằng: Merino, J, et al.
Được phát hành: (2005)

Thermal shock of ground and polished alumina and Al(2)O(3)/SiC nanocomposites
Bằng: Maensiri, S, et al.
Được phát hành: (2002)

Neutron diffraction measurements of residual stresses in alumina/SiC nanocomposites
Bằng: Todd, R, et al.
Được phát hành: (1997)

Relationship between wear rate, surface pullout and microstructure during abrasive wear of alumina and alumina/SiC nanocomposites
Bằng: Ortiz-Merino, J, et al.
Được phát hành: (2005)

Nanodispersoid and Interface in Sintered Si3N4-SiC Nanocomposites
Bằng: Koichi Niihara
Được phát hành: (2014-05-01)

THE PROPULSION OF SURFACE FLAWS BY ELASTIC INDENTATION TESTING
Bằng: Dai, D, et al.
Được phát hành: (1995)

Subsurface damage analysis by TEM and 3D FIB crack mapping in alumina and alumina/5vol.%SiC nanocomposites
Bằng: Wu, H, et al.
Được phát hành: (2003)

Hardness and indentation load-size effect in Al2O3-SiC nanocomposites
Bằng: Csehova, E, et al.
Được phát hành: (2011)

Progress in flaw growth and fracture toughness testing /
Bằng: National Symposium on Fracture Mechanics (6th : Philadelphia, 1972), et al.
Được phát hành: (1973)

Study on Indentation Experiments and Mechanical Behavior of RB-SiC
Bằng: Cheng Fan, et al.
Được phát hành: (2017-01-01)

Investigation of Variability of Flaw Strength Distributions on Brittle SiC Ceramic
Bằng: Jacques Lamon
Được phát hành: (2024-06-01)

Study on Notch Sensitivity and Failure of 3D Needled C/SiC Fracture Toughness
Bằng: LIU Bin, et al.
Được phát hành: (2022-04-01)

Sintering Behavior of Spark Plasma Sintered SiC with Si-SiC Composite Nanoparticles Prepared by Thermal DC Plasma Process
Bằng: Yeon-Tae Yu, et al.
Được phát hành: (2017-11-01)

Preliminary investigation of flash sintering of SiC
Bằng: Zapata-Solvas, E, et al.
Được phát hành: (2013)

Polishing and wear behaviour of sintered alumina-silicon carbide nanocomposites
Bằng: Cock, A, et al.
Được phát hành: (2001)

Effect of cenosphere and specimen crack lengths on the fracture toughness of Al6061-SiC composites
Bằng: E. Ashoka, et al.
Được phát hành: (2022-07-01)

Effect of BNNTs/matrix interface tailoring on toughness and fracture morphology of hierarchical SiCf/SiC composites
Bằng: Guangxiang Zhu, et al.
Được phát hành: (2019-12-01)

Effects of yttrium on the sintering and microstructure of alumina-silicon carbide "nanocomposites"
Bằng: Cock, A, et al.
Được phát hành: (2005)

Synthesis of cBN-hBN-SiC<sub>w</sub> Nanocomposite with Superior Hardness, Strength, and Toughness
Bằng: Lei Sun, et al.
Được phát hành: (2022-12-01)

Comparison of mechanical behavior of SiC sintered specimen to analysis of surface defects
Bằng: Tomić N.Z., et al.
Được phát hành: (2014-01-01)

Observation and simulation of indentation damage in a SiC-SiCfibre ceramic matrix composite
Bằng: Saucedo-Mora, L, et al.
Được phát hành: (2015)

Synthesis and Characterization of NiP-TiC-SiC Nanocomposite Coating via Electroless Process on Alumina Substrate
Bằng: Rusul Abd, et al.
Được phát hành: (2023-12-01)

Self lubrication of pressureless sintered SiC ceramics
Bằng: Wei Zhang, et al.
Được phát hành: (2020-11-01)

Simultaneously enhancing the toughness and strength of cemented TiB2 nanocomposites through doping SiC whisker and graphene
Bằng: Jialin Sun, et al.
Được phát hành: (2023-09-01)

On understanding the mechanical properties and damage behavior of Cf/SiC composites by indentation method
Bằng: Zhongwang Wang, et al.
Được phát hành: (2023-09-01)

Indentation-induced crack interaction in alumina ceramics
Bằng: Twigg, P, et al.
Được phát hành: (1996)

Nanostructure-dependent indentation fracture toughness of metal-organic framework monoliths
Bằng: Tricarico, M, et al.
Được phát hành: (2023)

Indentation fracture toughness of Aluminium-Graphite composites: influence of nano-particles
Bằng: Alqahtani Ibrahim, et al.
Được phát hành: (2025-01-01)

Indentation Fracture Toughness of Aluminium-Graphite Composites: Influence of Nano-particles
Bằng: Ibrahim Alqahtani, et al.
Được phát hành: (2024-10-01)