Microstructural scale strain localisation in nuclear graphite

Microstructural scale strain localisation in nuclear graphite

The surface strain fields evolved during disc compression tests on virgin IM1-24 were obtained via electronic speckle pattern interferometry (ESPI). A methodology for characterising strain localisation on a microstructural scale is presented, which provides a quantitative description of the damage l...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Joyce, MR, Marrow, T
Định dạng:	Conference item
Được phát hành:	2008

Những quyển sách tương tự

Observations of strain localisation and failure in nuclear graphite
Bằng: Joyce, MR, et al.
Được phát hành: (2007)

Observation of microstructure deformation and damage in nuclear graphite
Bằng: Joyce, MR, et al.
Được phát hành: (2008)

The microstructure of nuclear graphite binders
Bằng: Wen, K, et al.
Được phát hành: (2008)

Microstructural characterisation of nuclear grade graphite
Bằng: Jones, A, et al.
Được phát hành: (2008)

Microstructural modelling of nuclear graphite using multi-phase models
Bằng: Berre, C, et al.
Được phát hành: (2008)

Modelling damage in nuclear graphite
Bằng: Becker, T, et al.
Được phát hành: (2013)

Nanostructures of carbon in nuclear graphite
Bằng: Wen, K, et al.
Được phát hành: (2008)

Nanostructures of carbon in nuclear graphite
Bằng: Wen, K, et al.
Được phát hành: (2008)

Microcracks in nuclear graphite and highly oriented pyrolytic graphite (HOPG)
Bằng: Wen, K, et al.
Được phát hành: (2008)

Multifractal-based assessment of Gilsocarbon graphite microstructures
Bằng: Vertyagina, Y, et al.
Được phát hành: (2016)

A multi-scale three-dimensional Cellular Automata fracture model of radiolytically oxidised nuclear graphite
Bằng: Vertyagina, Y, et al.
Được phát hành: (2017)

Annealing of ion irradiation damage in nuclear graphite
Bằng: Lasithiotakis, M, et al.
Được phát hành: (2013)

Multi-scale modelling of nuclear graphite tensile strength using the Site-Bond lattice model
Bằng: Morrison, C, et al.
Được phát hành: (2016)

Strain Localisation and Fracture of Nuclear Reactor Core Materials
Bằng: Malcolm Griffiths
Được phát hành: (2023-05-01)

Characterization of heterogeneity and nonlinearity in material properties of nuclear graphite using an inverse method
Bằng: Lin, L, et al.
Được phát hành: (2008)

3D cellular automata fracture model for porous graphite microstructures
Bằng: Vertyagina, Y, et al.
Được phát hành: (2016)

The effects of microstructure on strength and fracture resistance of nuclear graphite
Bằng: Zillhardt, T
Được phát hành: (2021)

Crack propagation resistance and damage mechanisms in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2007)

IN-SITU OBSERVATION OF CRACK NUCLEATION IN NUCLEAR GRAPHITE BY DIGITAL IMAGE CORRELATION
Bằng: Li, H, et al.
Được phát hành: (2009)

Crack propagation resistance and damage mechanisms in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2006)

Research activities of the Nuclear Graphite Research Group - University of Manchester
Bằng: Marsden, B, et al.
Được phát hành: (2004)

X-ray tomography observation of crack propagation in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2006)

SEM and TEM data of nuclear graphite and glassy carbon microstructures
Bằng: José David Arregui-Mena, et al.
Được phát hành: (2023-02-01)

Research activities of the Nuclear Graphite Research Group at the University of Manchester, UK
Bằng: Marsden, B, et al.
Được phát hành: (2004)

Three-dimensional characterization and thermal property modelling of thermally oxidized nuclear graphite
Bằng: Babout, L, et al.
Được phát hành: (2008)

Mapping the evolution of density in 3D of thermally oxidised graphite for nuclear applications
Bằng: Babout, L, et al.
Được phát hành: (2006)

Damage, crack growth and fracture characteristics of nuclear grade graphite using the Double Torsion technique
Bằng: Becker, T, et al.
Được phát hành: (2011)

Data related to the mesoscopic structure of iso-graphite for nuclear applications
Bằng: März, B, et al.
Được phát hành: (2018)

On the damage and fracture of nuclear graphite at multiple length-scales
Bằng: Liu, D, et al.
Được phát hành: (2017)

Numerical modelling of the effects of porosity changes on the mechanical properties of nuclear graphite
Bằng: Berre, C, et al.
Được phát hành: (2006)

X-ray tomographic observations applied to porosity models for the thermal properties of oxidised nuclear graphite
Bằng: Babout, L, et al.
Được phát hành: (2007)

Study on Microstructure Evolution of Nuclear-grade Graphite after C Ion Irradiation
Bằng: GUO Lina;BIAN Wei;LIU Fanggang;HE Zhoutong;PENG Shunmi
Được phát hành: (2023-02-01)

The infiltration behavior and chemical compatibility of molten lead-bismuth eutectic in nuclear graphite at elevated temperature
Bằng: He, Z, et al.
Được phát hành: (2021)

Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens
Bằng: Shi, L, et al.
Được phát hành: (2004)

Synchrotron X-ray characterisation of crack strain fields in polygranular graphite
Bằng: Barhli, S, et al.
Được phát hành: (2017)

Microstructural characterization data for nuclear graphite samples generated during tribology testing in argon
Bằng: L. Vergari, et al.
Được phát hành: (2023-04-01)

Synchrotron X-ray Tomographic Quantification of Deformation Induced Strain Localisation in Semi-solid Al-15wt.% Cu
Bằng: Cai, B, et al.
Được phát hành: (2015)

Etoposide induces nuclear re-localisation of AID.
Bằng: Laurens J Lambert, et al.
Được phát hành: (2013-01-01)

Failure analysis of the effects of porosity in thermally oxidised nuclear graphite using finite element modelling
Bằng: Berre, C, et al.
Được phát hành: (2008)

Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens
Bằng: Shi, L, et al.
Được phát hành: (2008)