A phase field formulation for hydrogen assisted cracking

A phase field formulation for hydrogen assisted cracking

We present a phase field modeling framework for hydrogen assisted cracking. The model builds upon a coupled mechanical and hydrogen diffusion response, driven by chemical potential gradients, and a hydrogen-dependent fracture energy degradation law grounded on first principles calculations. The coup...

Szczegółowa specyfikacja

Opis bibliograficzny
Główni autorzy:	Martinez-Paneda, E, Golahmar, A, Niordson, CF
Format:	Journal article
Język:	English
Wydane:	Elsevier 2018

Podobne zapisy

A phase field model for hydrogen-assisted fatigue
od: Golahmar, A, i wsp.
Wydane: (2021)

A phase field model for high-cycle fatigue: total-life analysis
od: Golahmar, A, i wsp.
Wydane: (2023)

Applications of phase field fracture in modelling hydrogen assisted failures
od: Kristensen, PK, i wsp.
Wydane: (2020)

Accelerated high-cycle phase field fatigue predictions
od: Kristensen, PK, i wsp.
Wydane: (2023)

Strain gradient plasticity-based modeling of hydrogen environment assisted cracking
od: Martinez-Paneda, E, i wsp.
Wydane: (2016)

An assessment of phase field fracture: crack initiation and growth
od: Kristensen, PK, i wsp.
Wydane: (2021)

A phase field model for elastic-gradient-plastic solids undergoing hydrogen embrittlement
od: Kristensen, PK, i wsp.
Wydane: (2020)

Strain gradient plasticity modeling of hydrogen diffusion to the crack tip
od: Martinez-Paneda, E, i wsp.
Wydane: (2016)

A phase field formulation for dissolution-driven stress corrosion cracking
od: Cui, C, i wsp.
Wydane: (2020)

The role of plastic strain gradients in the crack growth resistance of metals
od: Martínez-Pañeda, E, i wsp.
Wydane: (2019)

A coupled phase field formulation for modelling fatigue cracking in lithium-ion battery electrode particles
od: Ai, W, i wsp.
Wydane: (2022)

A mechanism-based multi-trap phase field model for hydrogen assisted fracture
od: Isfandbod, M, i wsp.
Wydane: (2021)

On fracture in finite strain gradient plasticity
od: Martínez-Pañeda, E, i wsp.
Wydane: (2015)

A generalised, multi-phase-field theory for dissolution-driven stress corrosion cracking and hydrogen embrittlement
od: Cui, C, i wsp.
Wydane: (2022)

Computational predictions of hydrogen-assisted fatigue crack growth
od: Cui, C, i wsp.
Wydane: (2024)

A finite element framework for distortion gradient plasticity with applications to bending of thin foils
od: Martínez-Pañeda, E, i wsp.
Wydane: (2016)

Cohesive zone modelling of hydrogen assisted fatigue crack growth: the role of trapping
od: Fernández-Sousa, R, i wsp.
Wydane: (2022)

Phase field modelling of crack propagation in functionally graded materials
od: Hirshikesh, i wsp.
Wydane: (2019)

Progress and opportunities in modelling environmentally assisted cracking
od: Martinez-Paneda, E
Wydane: (2021)

Adaptive phase field modelling of crack propagation in orthotropic functionally graded materials
od: Martinez-Paneda, E, i wsp.
Wydane: (2020)

On the suitability of single-edge notch tension (SENT) testing for assessing hydrogen-assisted cracking susceptibility
od: Cupertino-Malheiros, L, i wsp.
Wydane: (2024)

A micro-mechanics based extension of the GTN continuum model accounting for random void distributions
od: Holte, I, i wsp.
Wydane: (2023)

Phase field cohesive zone modeling for fatigue crack propagation in quasi-brittle materials
od: Baktheer, A, i wsp.
Wydane: (2024)

A phase field-based framework for electro-chemo-mechanical fracture: crack-contained electrolytes, chemical reactions and stabilisation
od: Hageman, T, i wsp.
Wydane: (2023)

Steady-state fracture toughness of elastic-plastic solids: isotropic versus kinematic hardening
od: Juul, KJ, i wsp.
Wydane: (2019)

A phase-field chemo-mechanical model for corrosion-induced cracking in reinforced concrete
od: Korec, E, i wsp.
Wydane: (2023)

Generalised boundary conditions for hydrogen transport at crack tips
od: Martínez-Pañeda, E, i wsp.
Wydane: (2020)

Hydrogen-assisted fatigue crack growth: pre-charging vs in-situ testing in gaseous environments
od: Zafra, A, i wsp.
Wydane: (2023)

An FFT-based crystal plasticity phase-field model for micromechanical fatigue cracking based on the stored energy density
od: Lucarini, S, i wsp.
Wydane: (2023)

A microstructure-sensitive electro-chemo-mechanical phase-field model of pitting and stress corrosion cracking
od: Makuch, M, i wsp.
Wydane: (2024)

A generalised phase field model for fatigue crack growth in elastic–plastic solids with an efficient monolithic solver
od: Khalil, Z, i wsp.
Wydane: (2021)

Interaction of void spacing and material size effect on inter-void flow localization
od: Holte, I, i wsp.
Wydane: (2020)

Phase-field modeling of pitting and mechanically-assisted corrosion of Mg alloys for biomedical applications
od: Kovacevic, S, i wsp.
Wydane: (2023)

A phase field electro-chemo-mechanical formulation for predicting void evolution at the Li–electrolyte interface in all-solid-state batteries
od: Zhao, Y, i wsp.
Wydane: (2022)

Phase-field chemo-mechanical modelling of corrosion-induced cracking in reinforced concrete subjected to non-uniform chloride-induced corrosion
od: Korec, E, i wsp.
Wydane: (2023)

Analysis of the influence of microstructural traps on hydrogen assisted fatigue
od: Fernández-Sousa, R, i wsp.
Wydane: (2020)

Phase-field simulations opening new horizons in corrosion research
od: Martínez-Pañeda, E
Wydane: (2024)

Crack tip fields and fracture resistance parameters based on strain gradient plasticity
od: Shlyannikov, V, i wsp.
Wydane: (2020)

Mode I crack tip fields: strain gradient plasticity theory versus J2 flow theory
od: Martinez-Paneda, E, i wsp.
Wydane: (2019)

Computational modelling of hydrogen assisted fracture in polycrystalline materials
od: Valverde-González, A, i wsp.
Wydane: (2022)