A phase field formulation for hydrogen assisted cracking

A phase field formulation for hydrogen assisted cracking

We present a phase field modeling framework for hydrogen assisted cracking. The model builds upon a coupled mechanical and hydrogen diffusion response, driven by chemical potential gradients, and a hydrogen-dependent fracture energy degradation law grounded on first principles calculations. The coup...

書目詳細資料
Main Authors:	Martinez-Paneda, E, Golahmar, A, Niordson, CF
格式:	Journal article
語言:	English
出版:	Elsevier 2018

相似書籍

A phase field model for hydrogen-assisted fatigue
由: Golahmar, A, et al.
出版: (2021)

A phase field model for high-cycle fatigue: total-life analysis
由: Golahmar, A, et al.
出版: (2023)

Applications of phase field fracture in modelling hydrogen assisted failures
由: Kristensen, PK, et al.
出版: (2020)

Accelerated high-cycle phase field fatigue predictions
由: Kristensen, PK, et al.
出版: (2023)

Strain gradient plasticity-based modeling of hydrogen environment assisted cracking
由: Martinez-Paneda, E, et al.
出版: (2016)

An assessment of phase field fracture: crack initiation and growth
由: Kristensen, PK, et al.
出版: (2021)

A phase field model for elastic-gradient-plastic solids undergoing hydrogen embrittlement
由: Kristensen, PK, et al.
出版: (2020)

Strain gradient plasticity modeling of hydrogen diffusion to the crack tip
由: Martinez-Paneda, E, et al.
出版: (2016)

A phase field formulation for dissolution-driven stress corrosion cracking
由: Cui, C, et al.
出版: (2020)

The role of plastic strain gradients in the crack growth resistance of metals
由: Martínez-Pañeda, E, et al.
出版: (2019)

A coupled phase field formulation for modelling fatigue cracking in lithium-ion battery electrode particles
由: Ai, W, et al.
出版: (2022)

A mechanism-based multi-trap phase field model for hydrogen assisted fracture
由: Isfandbod, M, et al.
出版: (2021)

On fracture in finite strain gradient plasticity
由: Martínez-Pañeda, E, et al.
出版: (2015)

A generalised, multi-phase-field theory for dissolution-driven stress corrosion cracking and hydrogen embrittlement
由: Cui, C, et al.
出版: (2022)

Computational predictions of hydrogen-assisted fatigue crack growth
由: Cui, C, et al.
出版: (2024)

A finite element framework for distortion gradient plasticity with applications to bending of thin foils
由: Martínez-Pañeda, E, et al.
出版: (2016)

Cohesive zone modelling of hydrogen assisted fatigue crack growth: the role of trapping
由: Fernández-Sousa, R, et al.
出版: (2022)

Phase field modelling of crack propagation in functionally graded materials
由: Hirshikesh, et al.
出版: (2019)

Progress and opportunities in modelling environmentally assisted cracking
由: Martinez-Paneda, E
出版: (2021)

Adaptive phase field modelling of crack propagation in orthotropic functionally graded materials
由: Martinez-Paneda, E, et al.
出版: (2020)

On the suitability of single-edge notch tension (SENT) testing for assessing hydrogen-assisted cracking susceptibility
由: Cupertino-Malheiros, L, et al.
出版: (2024)

A micro-mechanics based extension of the GTN continuum model accounting for random void distributions
由: Holte, I, et al.
出版: (2023)

Phase field cohesive zone modeling for fatigue crack propagation in quasi-brittle materials
由: Baktheer, A, et al.
出版: (2024)

A phase field-based framework for electro-chemo-mechanical fracture: crack-contained electrolytes, chemical reactions and stabilisation
由: Hageman, T, et al.
出版: (2023)

Steady-state fracture toughness of elastic-plastic solids: isotropic versus kinematic hardening
由: Juul, KJ, et al.
出版: (2019)

A phase-field chemo-mechanical model for corrosion-induced cracking in reinforced concrete
由: Korec, E, et al.
出版: (2023)

Generalised boundary conditions for hydrogen transport at crack tips
由: Martínez-Pañeda, E, et al.
出版: (2020)

Hydrogen-assisted fatigue crack growth: pre-charging vs in-situ testing in gaseous environments
由: Zafra, A, et al.
出版: (2023)

An FFT-based crystal plasticity phase-field model for micromechanical fatigue cracking based on the stored energy density
由: Lucarini, S, et al.
出版: (2023)

A microstructure-sensitive electro-chemo-mechanical phase-field model of pitting and stress corrosion cracking
由: Makuch, M, et al.
出版: (2024)

A generalised phase field model for fatigue crack growth in elastic–plastic solids with an efficient monolithic solver
由: Khalil, Z, et al.
出版: (2021)

Interaction of void spacing and material size effect on inter-void flow localization
由: Holte, I, et al.
出版: (2020)

Phase-field modeling of pitting and mechanically-assisted corrosion of Mg alloys for biomedical applications
由: Kovacevic, S, et al.
出版: (2023)

A phase field electro-chemo-mechanical formulation for predicting void evolution at the Li–electrolyte interface in all-solid-state batteries
由: Zhao, Y, et al.
出版: (2022)

Phase-field chemo-mechanical modelling of corrosion-induced cracking in reinforced concrete subjected to non-uniform chloride-induced corrosion
由: Korec, E, et al.
出版: (2023)

Analysis of the influence of microstructural traps on hydrogen assisted fatigue
由: Fernández-Sousa, R, et al.
出版: (2020)

Phase-field simulations opening new horizons in corrosion research
由: Martínez-Pañeda, E
出版: (2024)

Crack tip fields and fracture resistance parameters based on strain gradient plasticity
由: Shlyannikov, V, et al.
出版: (2020)

Mode I crack tip fields: strain gradient plasticity theory versus J2 flow theory
由: Martinez-Paneda, E, et al.
出版: (2019)

Computational modelling of hydrogen assisted fracture in polycrystalline materials
由: Valverde-González, A, et al.
出版: (2022)