Quantitative in situ study of short crack propagation in polygranular graphite by digital image correlation

Quantitative in situ study of short crack propagation in polygranular graphite by digital image correlation

Hiển thị phiên bản (1) khác

This paper reports experimental observations that show non-irradiated Gilsocarbon polygranular nuclear graphite fits within the quasi-brittle class of materials. Such materials exhibit a degree of damage tolerance that depends on the stability of cracks that nucleate in the microstructure. Modelling...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Mostafavi, M, Marrow, T
Định dạng:	Journal article
Ngôn ngữ:	English
Được phát hành:	2012

Những quyển sách tương tự

Quantitative in situ study of short crack propagation in polygranular graphite by digital image correlation
Bằng: Mostafavi, M, et al.
Được phát hành: (2012)

Fracture behaviour of an anisotropic polygranular graphite (PGA)
Bằng: Mostafavi, M, et al.
Được phát hành: (2012)

Fracture behaviour of an anisotropic polygranular graphite (PGA)
Bằng: Mostafavi, M, et al.
Được phát hành: (2012)

Synchrotron X-ray characterisation of crack strain fields in polygranular graphite
Bằng: Barhli, S, et al.
Được phát hành: (2017)

Small-specimen testing, with image-based analysis, for crack propagation resistance in polygranular nuclear graphite
Bằng: Marrow, J, et al.
Được phát hành: (2022)

In situ mechanical loading and neutron Bragg-edge imaging, applied to polygranular graphite on IMAT@ISIS
Bằng: Zillhardt, TAC, et al.
Được phát hành: (2021)

In situ observation of crystal reorientation in polygranular graphite by synchrotron X-ray diffraction and neutron imaging
Bằng: Zillhardt, T, et al.
Được phát hành: (2023)

In situ measurement of the strains within a mechanically loaded polygranular graphite
Bằng: Marrow, T, et al.
Được phát hành: (2016)

Flexural strength and defect behaviour of polygranular graphite under different states of stress
Bằng: Mostafavi, M, et al.
Được phát hành: (2013)

Flexural strength and defect behaviour of polygranular graphite under different states of stress
Bằng: Mostafavi, M, et al.
Được phát hành: (2013)

In situ measurement of elastic and total strains during ambient and high temperature deformation of a polygranular graphite
Bằng: Liu, D, et al.
Được phát hành: (2020)

IN-SITU OBSERVATION OF CRACK NUCLEATION IN NUCLEAR GRAPHITE BY DIGITAL IMAGE CORRELATION
Bằng: Li, H, et al.
Được phát hành: (2009)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
Bằng: Marrow, T, et al.
Được phát hành: (2012)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
Bằng: Mostafavi, M, et al.
Được phát hành: (2013)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
Bằng: Mostafavi, M, et al.
Được phát hành: (2013)

A quantitative three-dimensional in situ study of a short fatigue crack in a magnesium alloy
Bằng: Marrow, T, et al.
Được phát hành: (2014)

A quantitative three-dimensional in situ study of a short fatigue crack in a magnesium alloy
Bằng: Marrow, T, et al.
Được phát hành: (2014)

In situ observation of crack nuclei in poly-granular graphite under ring-on-ring equi-biaxial and flexural loading
Bằng: Mostafavi, M, et al.
Được phát hành: (2011)

In situ observation of short fatigue crack propagation in oxygenated water at elevated temperature and pressure
Bằng: Duff, J, et al.
Được phát hành: (2013)

In situ observation of short fatigue crack propagation in oxygenated water at elevated temperature and pressure
Bằng: Duff, J, et al.
Được phát hành: (2013)

Temperature dependence of electrical resistivity, deformation, and fracture of polygranular graphite with different amounts of porosity
Bằng: C. Paraskevoulakos, et al.
Được phát hành: (2022-12-01)

Crack propagation resistance and damage mechanisms in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2007)

Crack propagation resistance and damage mechanisms in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2006)

X-ray tomography observation of crack propagation in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2006)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
Bằng: Vertyagina, Y, et al.
Được phát hành: (2014)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
Bằng: Vertyagina, Y, et al.
Được phát hành: (2014)

Crack propagation in fine grained graphites under mode I and mixed-mode loading, as observed in situ by microtomography
Bằng: Jin, X, et al.
Được phát hành: (2022)

In-situ observation of damage nucleation in graphite under biaxial flexural loading
Bằng: Mostafavi, M, et al.
Được phát hành: (2010)

In-situ observation of damage nucleation in graphite under biaxial flexural loading
Bằng: Mostafavi, M, et al.
Được phát hành: (2010)

Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens
Bằng: Shi, L, et al.
Được phát hành: (2004)

Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens
Bằng: Shi, L, et al.
Được phát hành: (2008)

Application of digital image correlation method to study crack propagation in concrete beam /
Bằng: 234629 Sia, Siaw Boon, et al.
Được phát hành: (2008)

A New Method to Measure Crack Extension in Nuclear Graphite Based on Digital Image Correlation
Bằng: Shigang Lai, et al.
Được phát hành: (2017-01-01)

Preliminary evaluation of digital image correlation for in-situ observation of low temperature atmospheric-induced chloride stress corrosion cracking in austenitic stainless steels
Bằng: Cook, A, et al.
Được phát hành: (2010)

Investigation of Crack Propagation and Healing of Asphalt Concrete Using Digital Image Correlation
Bằng: Navid Hasheminejad, et al.
Được phát hành: (2019-06-01)

Development of a Digital Image Correlation controlled fatigue crack propagation experiment
Bằng: Rethore J., et al.
Được phát hành: (2010-06-01)

New techniques for in-situ observations of crack growth behaviour
Bằng: Marrow, T
Được phát hành: (2008)

An approach to calculate the J-integral by digital image correlation displacement field measurement
Bằng: Becker, T, et al.
Được phát hành: (2012)

Three-dimensional in situ observations of short fatigue crack growth in magnesium
Bằng: King, A, et al.
Được phát hành: (2011)

Application of digital image correlation method to study crack propagation in concrete beam [electronic resource] /
Bằng: 234629 Sia, Siaw Boon, et al.
Được phát hành: (2008)