Characterization of nanostructured CdS film deposited at low growth rate using CBD technique

Cds film was deposited by chemical bath deposition (CBD) on commercial glass substrate at the constant bath temperature 72 o C. The deposition time was varied from 1 to 4 hours. The film growth rate varies from 0.89 nm to 0.26 nm. It was found that the adhesion was very good for all film deposition...