Characterization of nanostructured CdS film deposited at low growth rate using CBD technique
Cds film was deposited by chemical bath deposition (CBD) on commercial glass substrate at the constant bath temperature 72 o C. The deposition time was varied from 1 to 4 hours. The film growth rate varies from 0.89 nm to 0.26 nm. It was found that the adhesion was very good for all film deposition...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
National Institute of Materials Physics, National Institute of Optoelectronics
2010
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/13546/1/Characterization%20of%20nanostructured%20CdS%20film%20deposited%20at%20low%20growth%20rate%20using%20CBD%20technique.pdf |
| _version_ | 1825945257115648000 |
|---|---|
| author | Rizwan, Zahid Zakaria, Azmi Md Daud, Mohd Norizam Mohd Ghazali, Mohd Sabri Zamiri, Reza Noroozi, Monir |
| author_facet | Rizwan, Zahid Zakaria, Azmi Md Daud, Mohd Norizam Mohd Ghazali, Mohd Sabri Zamiri, Reza Noroozi, Monir |
| author_sort | Rizwan, Zahid |
| collection | UPM |
| description | Cds film was deposited by chemical bath deposition (CBD) on commercial glass substrate at the constant bath temperature 72 o C. The deposition time was varied from 1 to 4 hours. The film growth rate varies from 0.89 nm to 0.26 nm. It was found that the adhesion was very good for all film deposition times. Film thickness was measured by ellipsometer and ranges from 52.7 to 56 nm for all deposition times. XRD analyses show that the film was cubic with crystallite size from 38 to 45 nm. The optical energy band gap (E g), Urbach energy (E oo) and absorption coefficient (α) was calculated from the transmission spectral data.
|
| first_indexed | 2024-03-06T07:28:40Z |
| format | Article |
| id | upm.eprints-13546 |
| institution | Universiti Putra Malaysia |
| language | English |
| last_indexed | 2024-03-06T07:28:40Z |
| publishDate | 2010 |
| publisher | National Institute of Materials Physics, National Institute of Optoelectronics |
| record_format | dspace |
| spelling | upm.eprints-135462015-11-02T02:33:05Z http://psasir.upm.edu.my/id/eprint/13546/ Characterization of nanostructured CdS film deposited at low growth rate using CBD technique Rizwan, Zahid Zakaria, Azmi Md Daud, Mohd Norizam Mohd Ghazali, Mohd Sabri Zamiri, Reza Noroozi, Monir Cds film was deposited by chemical bath deposition (CBD) on commercial glass substrate at the constant bath temperature 72 o C. The deposition time was varied from 1 to 4 hours. The film growth rate varies from 0.89 nm to 0.26 nm. It was found that the adhesion was very good for all film deposition times. Film thickness was measured by ellipsometer and ranges from 52.7 to 56 nm for all deposition times. XRD analyses show that the film was cubic with crystallite size from 38 to 45 nm. The optical energy band gap (E g), Urbach energy (E oo) and absorption coefficient (α) was calculated from the transmission spectral data. National Institute of Materials Physics, National Institute of Optoelectronics 2010-06 Article PeerReviewed application/pdf en http://psasir.upm.edu.my/id/eprint/13546/1/Characterization%20of%20nanostructured%20CdS%20film%20deposited%20at%20low%20growth%20rate%20using%20CBD%20technique.pdf Rizwan, Zahid and Zakaria, Azmi and Md Daud, Mohd Norizam and Mohd Ghazali, Mohd Sabri and Zamiri, Reza and Noroozi, Monir (2010) Characterization of nanostructured CdS film deposited at low growth rate using CBD technique. Chalcogenide Letters, 7 (6). pp. 423-429. ISSN 1584-8663 http://www.chalcogen.ro/423_Zahid-Rizwan.pdf |
| spellingShingle | Rizwan, Zahid Zakaria, Azmi Md Daud, Mohd Norizam Mohd Ghazali, Mohd Sabri Zamiri, Reza Noroozi, Monir Characterization of nanostructured CdS film deposited at low growth rate using CBD technique |
| title | Characterization of nanostructured CdS film deposited at low growth rate using CBD technique |
| title_full | Characterization of nanostructured CdS film deposited at low growth rate using CBD technique |
| title_fullStr | Characterization of nanostructured CdS film deposited at low growth rate using CBD technique |
| title_full_unstemmed | Characterization of nanostructured CdS film deposited at low growth rate using CBD technique |
| title_short | Characterization of nanostructured CdS film deposited at low growth rate using CBD technique |
| title_sort | characterization of nanostructured cds film deposited at low growth rate using cbd technique |
| url | http://psasir.upm.edu.my/id/eprint/13546/1/Characterization%20of%20nanostructured%20CdS%20film%20deposited%20at%20low%20growth%20rate%20using%20CBD%20technique.pdf |
| work_keys_str_mv | AT rizwanzahid characterizationofnanostructuredcdsfilmdepositedatlowgrowthrateusingcbdtechnique AT zakariaazmi characterizationofnanostructuredcdsfilmdepositedatlowgrowthrateusingcbdtechnique AT mddaudmohdnorizam characterizationofnanostructuredcdsfilmdepositedatlowgrowthrateusingcbdtechnique AT mohdghazalimohdsabri characterizationofnanostructuredcdsfilmdepositedatlowgrowthrateusingcbdtechnique AT zamirireza characterizationofnanostructuredcdsfilmdepositedatlowgrowthrateusingcbdtechnique AT noroozimonir characterizationofnanostructuredcdsfilmdepositedatlowgrowthrateusingcbdtechnique |