Fatigue damage of 2024-T351 aluminium alloy friction stir welding joints. Part 2: fatigue damage
The characterisation of micro and macro mechanics in 2024-T351 (Al Alloy) FSW joints was conducted to identify the critical regimes for natural fatigue crack initiation in 2024-T351 Al Alloy FSW welded joints and was presented in Part 1. In this Part, the fatigue tests were performed. Scanning elect...