Fatigue damage mechanism of titanium in vacuum and in air

The fatigue damage of titanium has been studied on thin plate specimens subjected to alternating plane bending in two different environments: in vacuum (1.3 x 10-3 Pa) and in air. Fatigue properties of titanium were better in vacuum than in air. Fatigue damage was distinguished between the testing a...

Description complète

Détails bibliographiques
Auteurs principaux: Zahari, Nur Ismarrubie, Yussof, Hanafiah, Sugano, M.
Format: Article
Langue:English
Publié: Elsevier 2012
Accès en ligne:http://psasir.upm.edu.my/id/eprint/43108/1/Fatigue%20Damage%20Mechanism%20of%20Titanium%20in%20Vacuum%20and%20in%20Air.pdf