Delamination damage of carbon fiber-reinforced polymer composite laminates under cyclic shear-induced loading conditions

Interface delamination is a major failure mode induced by in-plane shear stress frequently encountered in carbon fiber-reinforce polymer (CFRP) composite laminates structures. This failure process under monotonic loading has been successfully described using cohesive zone model (CZM). Many previ...