Urease-carrying electrospun polyacrylonitrile mat for urea hydrolysis
Electrospinning was used to fabricate beadless microfibrous polyacrylonitrile (ePAN) mats with an average fiber diameter of 1448 ± 380 nm from a 10 wt.% PAN in dimethylformamide (DMF) dope solution at applied voltage of 18 kV and 20 cm fiber collection distance. Urease (EC 3.5.1.5) was then covalent...