Urease-carrying electrospun polyacrylonitrile mat for urea hydrolysis
Electrospinning was used to fabricate beadless microfibrous polyacrylonitrile (ePAN) mats with an average fiber diameter of 1448 ± 380 nm from a 10 wt.% PAN in dimethylformamide (DMF) dope solution at applied voltage of 18 kV and 20 cm fiber collection distance. Urease (EC 3.5.1.5) was then covalent...
Main Authors: | Daneshfar, Aref, Matsuura, Takeshi, Emadzadeh, Daryoush, Pahlevani, Zahra, Ismail, Ahmad Fauzi |
---|---|
Format: | Article |
Published: |
Elsevier
2015
|
Subjects: |
Similar Items
-
The study of pH, temperature, reusability, and storage stabilty of urease immobilized on electrospun polyacrylonitrile mat
by: Daneshfar, Aref
Published: (2014) -
The study of pH, temperature, reusability, and storage stability of urease immobilized on electrospun polyacrylonitrile mat /
by: Aref Daneshfar, 1986- author, et al.
Published: (2014) -
The study of pH, temperature, reusability, and storage stability of urease immobilized on electrospun polyacrylonitrile mat [electronic resource] /
by: Aref Daneshfar, 1986-
Published: (2014) -
A novel thin film nanocomposite reverse osmosis membrane with superior anti-organic fouling affinity for water desalination
by: Emadzadeh, Daryoush, et al.
Published: (2015) -
Synthesis, characterization and optimization of polyacrylonitrile electrospun nanofiber membranes /
by: Agung Mataram, 1979-, et al.
Published: (2012)